| Development and Application of LF Refining PreMelted Slag Without CaF2 |
| PAN Yifang1,LING Zunfeng1,WANG Baoming1,LI Shuqing1,WANG Zhenfeng2 |
| 1. Tianjin Iron and Steel Co., Ltd., Tianjin 300301, China;2. Department of Material Science and Engineering, Zhengzhou 450052, Henan, China |
|
|
|
|
Abstract In order to avoid the fluorine pollution, the LF refining premelted CaOAl2O3MgOSiO2 slag without CaF2 was developed based on the molten slag theory. The industrial practice showed that the slag was suitable for the BOFLFCC route to produce oilwell pipe steel such as 37Mn5 and 34Mn5, etc, according to the standard of API.5CT of USA, and the operation period of LF refining was decreased from 42 min to 35 min, establishing the foundation of high efficiency production and short production cycle. Meanwhile the slag, compared with the slag with CaF2, has good properties for desulphurization, deoxidation, and arc submerging, quick slag forming at the beginning of refining and foaming, as well as the advantages of lower lining erosion and no pollution of fluorine.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
Da‑peng Li, Hua‑zhang Wu, Hai‑feng Wang, Hong Li. Growth of solidified shell in bloom continuous casting mold of hypo-peritectic steel based on a FeS tracer method[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(7): 782-787. |
| [2] |
Jian-ming Su, Zhi-he Dou, Ting-an Zhang, Yan Liu. Kinetics of hot metal desulfurization by bottom blowing magnesium vapor[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(4): 392-401. |
| [3] |
ZHANG Wei-li1,WU Sheng-li1,HU Zhong-jie1,2. Statistical analysis of factors affecting desulfurization rate of activated coke for sintering flue gas[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 281-288. |
| [4] |
YIN Chuan-lei, YANG Li-mei, TIAN Chun-yang, MA Jian-chao. Analysis of KR hot metal desulfurizer escaped and slag agglomeration in agitator[J]. Iron and Steel, 2020, 55(1): 34-37. |
| [5] |
LU Yanan,WU Shengli,WANG Laixin,KOU Mingyin. Analysis of chemical compositions of slag affecting #br#
desulphurization in hot metal of COREX process[J]. Iron and Steel, 2019, 54(9): 33-38. |
| [6] |
XIAO Zunhu1，LIU Peng2，XU Gangjun2，ZHOU Junjun2，SUI Yafei2. Selection of calcium treatment technology of LF #br#
refining for different steel[J]. Iron and Steel, 2019, 54(9): 62-72. |
|
|
|
|
2006, Vol. 41 