Formation and Elimination of Red Scale on Hot Rolled Strip |
YU Yang1,2,TANG Shuai1,GUO Xiaobo2,GUAN Ju2,WANG Guodong1,LIU Jie2 |
1. The State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China;2. Hot Rolling Mill of Ansteel, Anshan 114021, Liaoning, China |
|
|
Abstract In order to eliminate the red scale on surface of hot rolled strip, the descaling and rolling experiments in lab and industrial trials were carried out. The evolution of red scale on hot rolled piece during descaling and hot rolling was analyzed by SEM and EDX. The formation mechanism of red scale was described and the optimized hot rolling parameters were proposed. After adopting the process rounte of descaling and rolling at high temperature and coiling at low temperature, red scale on surface of product was effectively removed and product quality at Ansteel was greatly improved.
|
Received: 01 January 1900
|
|
|
|
[1] |
SUN Xi-shun,LIANG Jing-zhao. Causes analysis of strip?edge?upwarping of 65Mn hot rolled coil[J]. Chinese Journal of Iron and Steel, 2015, 33(1): 48-50. |
[2] |
DING Bo,DING Mei-liang,GUAN Jian-hui,MAO Yong-ming. Analysis and Countermeasure for Descaling Indivisibility of Oxide Scale[J]. Iron and Steel, 2013, 48(6): 50-53. |
[3] |
GUO Xiangyu,LI Taiquan,SHEN Anming,PAN Shumin. Analysis and Improvement of Edge Cracks of Hot Rolled Coil[J]. Chinese Journal of Iron and Steel, 2011, 1(2): 35-40. |
[4] |
. Development of Economic-type X70 Linepipe Steel Hot Strip[J]. Chinese Journal of Iron and Steel, 2010, 22(05): 51-51. |
|
|
|
|