Analysis of Thermal Performance of Blast Furnace Cast Copper Staves |
SHI Lin1,2,CHENG Susen1,RUAN Xinwei3,XU Liangyou3 |
1. Metallurgy and Ecology Engineering School, University of Science and Technology of Beijing, Beijing 100083, China;2. Mathematics and Physics School, University of Science and Technology of Inner Mongolia, Baotou 014010, Neimenggu, China;3.Shaoxin Shuguang Machine Co., Ltd., Shaoxing 312065, Zhejiang China |
|
|
Abstract The thermal properties and deformation of new type cast copper stave with buried copper pipe were studied. The result shows that there is no difference in thermal properties between cast copper stave and rolled copper stave. The cooling capacity of cast one is very good. There is no air gap between wall and buried copper pipe. Based on the finite element analysis, the temperature distribution, stress and strain of cast copper stave at high temperature were calculated with the method of thermostructure coupling and calculated data were almost identical with measured. The result indicates that both the temperature and the stress of copper stave under BF operating condition are insufficient to cause cracking. The cast copper stave can satisfy the requirements of long campaign.
|
Received: 01 January 1900
|
|
|
|
[1] |
ZHU De-qing1,TIAN Hong-yu1,PAN Jian1,LIAO Hui2,GUO Zheng-qi1,XUE Yu-xiao1. Comprehensive utilization status and progress of low-grade laterite nickel ore[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 351-362. |
[2] |
WANG Kun1,LIU Xiao-jie1,LIU Er-hao2,LI Hong-yang1,LIU Song1,LV Qing1. Core temperature prediction model based on AdaBoost algorithm[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 363-369. |
[3] |
RONG Tao, TANG Hui-qing, FAN Kai, SUN Yan-jun. Applying high-carbon metallic briquette in blast furnace for coke saving[J]. Iron and Steel, 2020, 55(5): 10-19. |
[4] |
ZHANG Jian-liang, SUN Min-min, LI Ke-jiang, LI Hong-tao. Present situation and prospect of dissolution behavior of metallurgical coke in blast furnace hot metal[J]. Iron and Steel, 2020, 55(4): 1-11. |
[5] |
WANG Jin-liang, DAI Xi, ZHANG Wei, GONG Shu-shan, ZHOU Guo-zhi, ZHANG Wen-hai. Advances of non-blast furnace flash iron-making researches[J]. Iron and Steel, 2020, 55(4): 100-105. |
[6] |
ZHANG Xiao-hua, ZHAO Kai, BAI Geng-chen, ZHANG Yu-zhu, GAO Jian-jun, ZHANG Ying-yi. Thermal analysis of rotary kiln-oxygen combustion melting furnace under multi-constraint conditions[J]. Iron and Steel, 2020, 55(3): 9-15. |
|
|
|
|