Influence of Flux Injection Through Tuyeres on Burden SofteningMelting Properties and Primary Slag Properties |
FU Lianchun1,2,BI Xuegong1,ZHOU Guofan1, HU Tao3,XING Jiantong3,SONG Shuting3 |
1Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China;2Wuhan Iron and Steel Corporation (Group), Wuhan 430083, Hubei, China;3Anyang Iron and Steel Corporation, Anyang 455004, Henan, China |
|
|
Abstract The influence of basic flux injection through the tuyeres on softeningmelting properties of blast furnace burden and properties of primary slag was investigated in laboratory. The results show that with the decrease of burden basicity, the meltdown temperature was slightly decreased, the FeO content in meltdown primary slag was substantially increased, and the fluidity of primary slag was improved. Moreover, it was found that excessive high basicity of sinter would enlarge the basicity difference between meltdown primary slag and bosh primary slag, worsening slag stability. Theoretical calculation showed that by applying the technique of flux injection through the tuyeres, the blast furnace productivity could be improved.
|
Received: 01 January 1900
|
|
|
|
[1] |
MA Li-ming,ZHANG Jian-liang,WU Sheng-li,LIU Zheng-jian,WANG Yao-zu,XU Chen-yang. Treatment of vanadiumtitanium magnetite based on fluxed green ball composite agglomeration process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 462-469. |
[2] |
ZHU De-qing1,TIAN Hong-yu1,PAN Jian1,LIAO Hui2,GUO Zheng-qi1,XUE Yu-xiao1. Comprehensive utilization status and progress of low-grade laterite nickel ore[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 351-362. |
[3] |
WANG Kun1,LIU Xiao-jie1,LIU Er-hao2,LI Hong-yang1,LIU Song1,LV Qing1. Core temperature prediction model based on AdaBoost algorithm[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 363-369. |
[4] |
RONG Tao, TANG Hui-qing, FAN Kai, SUN Yan-jun. Applying high-carbon metallic briquette in blast furnace for coke saving[J]. Iron and Steel, 2020, 55(5): 10-19. |
[5] |
ZHANG Jian-liang, SUN Min-min, LI Ke-jiang, LI Hong-tao. Present situation and prospect of dissolution behavior of metallurgical coke in blast furnace hot metal[J]. Iron and Steel, 2020, 55(4): 1-11. |
[6] |
WANG Jin-liang, DAI Xi, ZHANG Wei, GONG Shu-shan, ZHOU Guo-zhi, ZHANG Wen-hai. Advances of non-blast furnace flash iron-making researches[J]. Iron and Steel, 2020, 55(4): 100-105. |
|
|
|
|