Study on Inclusions of 45A Caster |
ZHAI Jun WU Wei |
|
|
|
Abstract In order to determine the inclusions of 45A Caster ,in this paper ,with the help of metallographic observation、SEM and big sample electrolysis ,slab inclusion type, shape, dimension and distribution of arc caster have been studied .The results showed that:the whole control level of inclusion is well.The average of the amount of inclusions is 22.2mm-2,but in the middle of the caster inclusions is 25.8mm-2;With the help of big sample electrolysis,SEM,found that the total amount of inclusions of cast is 2.23mg/10kg,and inclusions is more than 300μm.Large inclusion come from mould fluxes、oxidation products、tundish covering flux and so on.
|
Received: 28 October 2008
|
|
|
|
[1] |
LAN Peng, TIE Zhan-peng, ZHANG Wei, MIAO Hong-sheng, YAN Qing-zhong, ZHANG Jia-quan. Research progress on spot segregation defects in continuously cast semi-products[J]. Iron and Steel, 2020, 55(2): 11-22. |
[2] |
LIN Peng,ZHANG Hong-cai,LIU Ying,XU Zheng-zhou. Cause analysis of surface crack defects of gear steel 20CrNiMo rolled product[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(2): 40-. |
[3] |
. Analysis and control of slag inclusion defect of low carbon steel slab[J]. , 2020, 45(2): 0-0. |
[4] |
XIE shizheng. Effect of roller EMS on macrostructure and properties of high strength steel[J]. , 2020, 45(1): 0-0. |
[5] |
AI Xingang,HAN Dong,LI Shengli,LIU Haixiao,. Production practice and prospect of external #br# liquid mold flux in continuous casting[J]. Iron and Steel, 2019, 54(8): 132-136. |
[6] |
LI Hongguang,DENG Tongwu,CHEN Liang,GUO Yuehua. Analysis and control of edge crack in high strength and #br#
high weathering steel YQ450NQR1[J]. Iron and Steel, 2019, 54(8): 169-173. |
|
|
|
|