Study on High Strength Deep Drawing Cold Rolled Steel Sheets 170P1 |
YIN Xiandong1,2,KANG Yonglin1,JIANG Qiwu2,LIU Rendong2,SUN Daqing2 |
1. Material Science and Engineering College, University of Science and Technology Beijing, Beijing 100083, China; 2. Angang New Steel Co.,Ltd.,Angang Group Corporation, Anshan 114003, Liaoning, China |
|
|
Abstract Histrength IF steel(170P1) produced by two hot rolling processes(normal and hot rolling in ferrite area) was studied. The results indicate that rvalue of Histrength IF steel hot rolled in ferrites area is up to 2.1. The qualification rate of the wings fabricated from the sheets produced in this way reaches 100%.
|
Received: 01 January 1900
|
|
|
|
[1] |
SUN Zhi-peng, XU Yan, SONG Zu-feng. Concrete manifestation and cause analysis of the abnormal r-value of the tensile testing machine[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(1): 24-. |
[2] |
XU Yan, SUN Zhi-peng, SONG Zu-feng. Elimination of r-value anomaly of width extensometer by linear fitting method[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(1): 28-. |
[3] |
ZHU Rui-qi,SONG Xin-li,ZHENG Ai-qin,CHEN Rong-dong,JIA Juan,FAN Li-xia. Strain hardening and microstructure characteristic of high strength IF bearing phosphorus steel[J]. Iron and Steel, 2018, 53(2): 55-59. |
[4] |
XIA Ming- sheng,LI Gui- lan,ZHANG Hong- bo,TIAN Zhi- ling,HAN Bing. Microstructures and properties of phosphorus- containing high strength cold rolled and annealed IF steels[J]. Chinese Journal of Iron and Steel, 2015, 27(12): 54-57. |
[5] |
WANG Chang,YU Yang,WANG Lin,CHEN Jin,XU Hai-wei. Research on the Factors Inducing Strip Fracture of High Strength IF Steel Containing Phosphorus During Straightening Process[J]. Iron and Steel, 2014, 49(5): 81-87. |
[6] |
LEI Zhe,LIU Guang-zu,YANG Zheng. Recrystallization Behavior of the MGH754 Cold-Rolled Sheet[J]. Chinese Journal of Iron and Steel, 2013, 25(05): 49-53. |
|
|
|
|