| Preliminary Study on Blast Furnace Dust Injection Into Blast Furnace |
| XU Hui1，YUAN Xingting1，WANG Xiaoming1，ZOU Zongshu1，LI Songbai2 |
| 1. College of Materials and Metallurgy, Northeastern University, Shenyang 110004, Liaoning， China； 2. Zhangdian Iron and Steel Company, Zibo 255007, Shandong， China |
|
|
|
|
Abstract Blast furnace dust contains a great deal of iron and carbon, and it causes serious pollution without disposal, thus it may be an effective disposal method to inject the dust back into the blast furnace using the popular pulverized coal injection equipment. Considering the possible change of slag basicity, sulfur content in hot metal, theoretical combustion temperature, and coke ratio inside the furnace with dust injection, a mass balance and local heat balance model was developed to calculate the change of coke ratio, slag basicity and theoretical combustion temperature with dust injection which provides theoretical basis for blast furnace operation and industrial test was carried out to confirm the idea and model. The results show that, with the increase of dust injection rate, the coke ratio and slag basicity decreased significantly while the theoretical combustion temperature did not change very much, and these changes could be handled by adjusting the ratio of sinters to pellets. Besides, with the increase of dust injection rate, the permeability of blast furnace decreased a little and blowing pressure was increased. In general, blast furnace dust injection into blast furnace is feasible.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
ZHU De-qing1,TIAN Hong-yu1,PAN Jian1,LIAO Hui2,GUO Zheng-qi1,XUE Yu-xiao1. Comprehensive utilization status and progress of low-grade laterite nickel ore[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 351-362. |
| [2] |
WANG Kun1,LIU Xiao-jie1,LIU Er-hao2,LI Hong-yang1,LIU Song1,LV Qing1. Core temperature prediction model based on AdaBoost algorithm[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 363-369. |
| [3] |
RONG Tao, TANG Hui-qing, FAN Kai, SUN Yan-jun. Applying high-carbon metallic briquette in blast furnace for coke saving[J]. Iron and Steel, 2020, 55(5): 10-19. |
| [4] |
ZHANG Jian-liang, SUN Min-min, LI Ke-jiang, LI Hong-tao. Present situation and prospect of dissolution behavior of metallurgical coke in blast furnace hot metal[J]. Iron and Steel, 2020, 55(4): 1-11. |
| [5] |
WANG Jin-liang, DAI Xi, ZHANG Wei, GONG Shu-shan, ZHOU Guo-zhi, ZHANG Wen-hai. Advances of non-blast furnace flash iron-making researches[J]. Iron and Steel, 2020, 55(4): 100-105. |
| [6] |
ZHANG Xiao-hua, ZHAO Kai, BAI Geng-chen, ZHANG Yu-zhu, GAO Jian-jun, ZHANG Ying-yi. Thermal analysis of rotary kiln-oxygen combustion melting furnace under multi-constraint conditions[J]. Iron and Steel, 2020, 55(3): 9-15. |
|
|
|
|
2008, Vol. 43 