Kinetics of Grain Growth in 6Cr21Mn10MoVNbN Valve Steel |
YU Shichang1,WU Shenqing1,GONG Youjun2,GONG Yuansheng2,LIAN Mingsheng2 |
1. Department of Material Science and Engineering, Southeast University, Nanjing 210096, Jiangsu, China; 2. Technology Center of Jiangsu Shenyuan Special Steel Company, Ltd., Xinghua 225722, Jiangsu, China |
|
|
Abstract Grain growth and its kinetics during solid solution treatment of 6Cr21Mn10MoVNbN steel in a temperature range from 1000 ℃ to 1250 ℃ were investigated. The experimental results show that the dispersed carbonitride in the steel greatly restrains grain growth. The grain size and Rockwell hardness are decreased a little by solid solution treatment at the temperature below grain coarsening temperature(1150 ℃) due to undissolved carbonitride, but grain grow rapidly and Rockwell hardness decreases quickly by solid solution at >1150 ℃. Grain growth increases exponently with the increasing solid solution treatment temperature. At the temperature from 1050 ℃ to 1100 ℃, the activation energy value for grain growth is 189.9 kJ/mol, which means that the grain growth mechanism is self-diffusion controlling process, and the grain growth kinetics equation is given.
|
Received: 01 January 1900
|
|
|
|
[1] |
BI Chuan-guang, HUANG Chun-chao, NING Xiao-jun, ZHANG Jian-liang, WANG Guang-wei, PENG Zheng-fu. Best ratio of semi-coke for blast furnace injection[J]. Iron and Steel, 2020, 55(6): 25-32. |
[2] |
JIANG Yue-yue, WANG Zhao-dong, DENG Xiang-tao. Effect of trace rare earth Ce on martensitic transformation behavior of ultra-high strength low alloy steel[J]. Iron and Steel, 2020, 55(6): 84-90. |
[3] |
LIU Ke, HAN Yi-hua, YANG Fan, ZHU Li-guang. Effect of MgO on microstructure of CaO-Al2O3 based quaternary system mold fluxes[J]. Iron and Steel, 2020, 55(5): 52-58. |
[4] |
CAO Yun-fei, YU Wei, LIU Min, JIANG Rui, WANG Chun. Austenite grain growth model of 38MnSiVS bearing microalloyed forging steel[J]. Iron and Steel, 2020, 55(5): 103-108. |
[5] |
XIAO Shao-bin, WANG Wei, LIU Tian-yu, ZHANG Qin, LÜ Zhi-qing. Effects of vacancies and C atoms on mechanical properties of Fe grain boundary[J]. Iron and Steel, 2020, 55(4): 75-81. |
[6] |
YANG Chen-xing1,2,WU Zhi-wei1,2,YANG Mao-sheng2,ZHAO Kun-yu1. Microstructure and mechanical properties of Ni-Cr bearing alloy in solution aging treatment[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(3): 242-252. |
|
|
|
|