Influence of Superhigh Basicity on Sinter Properties and Sintering Parameters |
JIANG Dajun1,HE Muguang1,GAN Qin2,HE Qun2 |
1Ironmaking Plant of Panzhihua Iron & Steel Co., Panzhihua 617024, Sichuan, China; 2Academe of Panzhihua Iron & Steel Co., Panzhihua 617024, Sichuan, China |
|
|
Abstract The experiment was performed on superhigh basicity sintering, to find out reasonable parameters, SiO2 content and intensification measures in laboratory. The results showed, in the basicity range of 2032, the ISO tumbler index and utilization coefficient was enhanced, sintering velocity increased, yield decreased with the increase of basicity. In the range of 2028 all the indexes were increassd almost linearly, but part of indexes went downward after basicity exceeding 28, so 28 is the most reasonable basicity.With the increase of basicity, titanium magnetite and hematite content was decreased, ferrite content increased, perovskite increased a little, silicate did not greatly change, reducibility(RI) and low temperature breakdown index(RDI) were improved. Softenning and melting temperature were increased, cohesive zone and dropping zone were narrowed down improving the blast furnace permeability. At a basicity of 28, an experiment for optimizing parameters by orthogonal method was performed. The results showed that it is neccessary to increase basicity from 24 to 28 in production with 50%, SiO2 but the basic condition is to rise TFe, lower SiO2 and TiO2 in VTi magnetite concentrate.
|
Received: 01 January 1900
|
|
|
|
[1] |
DU Liang, HAN Xiu-li, ZHANG Quan-sheng, ZHOU Xiang, YANG Hong-da, WANG Ying. Quantitative relation between mineralogical structure and metallurgical properties of sinter of import iron ore[J]. Iron and Steel, 2020, 55(6): 38-45. |
[2] |
HU Chang-qing,WANG Xiao-lei,SHI Xue-feng,WANG Zhi-xing,HAN Wei-gang. Effect of alkalinity and MgO content on mineral composition and microstructure of FeOx-SiO2-CaO-MgO-Al2O3 system[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 103-110. |
[3] |
LI Sheng, HE Zhi-jun, LI Yun-fei, QIU Shuang, ZHAN Wen-long, BAI Bing-yang. Metallurgical properties of furnace charge under different conditions of pellet ore and block ore addition[J]. Iron and Steel, 2020, 55(1): 6-11. |
[4] |
NIU Lele,LIU Zhengjian,ZHANG Jianliang,ZHANG Zongwang, WANG Yaozu,DU Chengbo. Effect of mineral composition of iron ore on metallurgical properties of sinter[J]. Iron and Steel, 2019, 54(9): 27-32. |
[5] |
YANG Nan,GUO Xing-min. Effect of SiO2 on composition and microstructure of crystal products of CaOFe2O3 melt[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 712-717. |
[6] |
YI Jinquan,ZENG Kai,XING Baoying,WU Wanping,ZHAI Tingting. Investigation and numerical simulation on weld bonding #br#
process for SPCC coldrolled steel[J]. Iron and Steel, 2019, 54(7): 93-97. |
|
|
|
|