Effects of Hot Deformation on γ→α Isothermal Transformation for High Niobium Low Carbon Steel |
CAO Jian-chun |
|
|
|
Abstract Using thermal simulation tester,austenite to ferrite isothermal transformation for a low carbon high niobium steel with and without hot deformation was investigated.It was obtained that curves of austenite to ferrite isothermal transformation at 700℃ for the tested steel in un-deformation, deformation 20% and 30% at 875℃,respectively. Influence of hot deformation and niobium on was discussed. The results show that the ferrite transformation is accelerated by hot deformation,because incubation period of the transformation is shortened by hot deformation,and the kinetics of austenite to ferrite isothermal transformation for high niobium steel is two stage that is ferrite transformation rate is lower in the first period and is higher in the second.
|
Received: 18 December 2009
|
|
|
|
[1] |
CHEN Yu-xiang1,2,LI Tao1,GONG Zhi-hua1,2,ZHAO Ji-qing2,YANG Gang2. Establishment of recrystallization kinetics equation and constitutive equation of 2Cr11Mo1VNbN steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 150-158. |
[2] |
SHEN Bin-bin, ZHENG Yan. AnalysisofHRB400Nbhotdeformationprocessparameters[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(4): 12-13. |
[3] |
GONG Zhi-hua1,2, HE Zhen3, BAO Han-sheng1, YANG Gang1. Hot deformation behavior of 2Cr12NiMo1W1V heat resistant steel used for supercritical steam turbine blades[J]. Iron and Steel, 2019, 54(3): 63-68. |
[4] |
MEI Rui-bin,,BAO Li,DU Yong-xia,ZHANG Xin,LI Chang-sheng,LIU Xiang-hua. Constitutive equations of Fe-6.5%Si steel at high deformation temperature[J]. Iron and Steel, 2018, 53(6): 98-102. |
[5] |
WANG Jing- zhong,,LIU A- jiao,,PANG Yu- hua,BAO Han- sheng. Hot deformation behavior of 07Cr25Ni21NbN austenitic heat resistant steel modified using 0. 3% vanadium[J]. , 2018, 30(5): 379-385. |
[6] |
WANG Qing- juan,LI Xiang- jun,REN Yao- jia,ZHOU Hai- xiong. Effect of initial state on hot deformation behavior of 65 wire rod[J]. , 2018, 30(12): 998-1005. |
|
|
|
|