| OneStep Direct Reduction of Damp Milled Magnetite Concentrate Pellets |
| ZHU Deqing1,XU Xiaofeng1,OU Yingqin2,ZHOU Wei3，PAN Jian1 |
| 1. School of Mineral Processing and Bioengineering, Central South University, Changsha 410083, Hunan,China; 2. Changtian International Engineering Corporation, MCC， Changsha 410001, Hunan, China; 3. Xinjiang Zijin Mining Industry Co., Ltd., Urumqi 830000, Xinjiang, China |
|
|
|
|
Abstract The direct reduction of magnetite pellets of 69.21%70.86% Fet, was conducted.The pellets were made from damp milled concentrate to increase strength of green balls, lower binder dosage and reduce fines generated during drying and handling dried balls.For the magnetite concentrate pretreated by damp milling for 4 min and balling at 7.2% moisture for 15 min,the drop number of green balls were increased from 3.8 times to 13.7 times from 0.5 meters and fines fraction of dried balls was reduced from 10.98% to 2.98%, respectively.The compressive strength of pellets preheated at 800 ℃ for 10 min was raised from 466 Newton to 581 Newton, while the metallization degree was almost the same compared with that made from magnetite concentrate prepared without damp milling.The pilot direct reduction was performed to stimulate gratekiln process. The results are as follows: Fet of DRI 93.91%,metallization degree 9599%, sulphur content lower than 0.01%, magnetic powder rate 0.75%096% and reductant coal rate 808.5859.3 kg/t.Such DRI is a high quality charge for electric arc furnace steel making.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
CHENG Xiang-kui, ZHAO Ying-tao, ZHAO Xu, WANG Jun, HUANG Xiao-li, PU Chun-lei. Preparation of V-Ti magnetite ore basic pellet containing NaOH[J]. Iron and Steel, 2020, 55(6): 33-37. |
| [2] |
ZHOU Ming-shun, WANG Yi-dong, ZHAO Dong-ming, HAN Hong-liang,LI Xian-chun, LU Li-ming. Development on sintering technologies with high proportion of magnetite concentrates[J]. Iron and Steel, 2020, 55(5): 1-9. |
| [3] |
FAN Jianjun, GUO Yufeng, ZANG Long, SHI Yonglin, LI Haokun, ZHENG Fuqiang. Effect of basicity on properties of pellets produced by ultra finesized iron concentrate[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(5): 440-445. |
| [4] |
LIU Cheng-xin，YU Jun-jie，ZHANG Ze-qiang，ZHANG Han-quan. Influence of damp milling on properties of artificial magnetite pellets[J]. Iron and Steel, 2018, 53(1): 17-23. |
| [5] |
ZHU De- qing，XU Meng- jie，PAN Jian，YANG Cong- cong，TIAN Hong- yu. Experimental research to improve ballability of ultrafine concentrate[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 704-710. |
| [6] |
DING Shan， XUE Qing-guo， SHE Xue-feng， WANG Guang， NING Xiao-yu， WANG Jing-song. Effect of CaCO3 on Direct Reduction-Smelting Separation of Vanadium-Bearing Titanomagnetite Concentrate[J]. Iron and Steel, 2014, 49(8): 15-20. |
|
|
|
|
2007, Vol. 42 