study on oxidation resistant of new austenite stainless steel |
Jack |
|
|
|
Abstract The high-temperature oxidation resistance of new austenitic stainless steel NH4 in air over the temperature range of 700℃~1000℃ was studied by using the way of gain weight. The surface morphology、constituent and micro-structure of the oxidation scale was analyzed by using XRD、SEM and EDX techniques. Experimental result indicated that the average oxidation speed of NH4 were 0.064 g/(m2 h)(700℃),0.083 g/(m2 h)(900℃)and0.2786 g/(m2 h)(1000℃).The compositions of oxide included outer Cr2O3 film and inner SiO2 film at 700℃ and 900℃. While at 1000℃ the oxide layer was a mixture of Cr2O3、SiO2 and Al2O3. At high temperature SiO2 layer was formed before Cr2O3 layer, and SiO2 layer was in favor of the formation of Cr2O3 layer.
|
Received: 06 November 2009
|
|
|
|
[1] |
DAI Xin-yu, FANG Xu-dong, XU Fang-hong, WEI Ying-hui, HOU Li-feng, DU Hua-yun. Research progress on low cycle fatigue properties of austenitic heat resistant steel[J]. Iron and Steel, 2020, 55(3): 58-67. |
[2] |
ZHANG Si-yuan1,2,LONG Mu-jun1,2,AI Song-yuan1,2,TAN Kai1,2,CHEN Deng-fu1,2,HUANG Yun-wei1,2. Oxidation behavior of continuous casting slabs and its effect on temperature during cooling process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 129-134. |
[3] |
LI Bai- song,,CHEN Wen- zhi,ZHAO Pei. Oxidation behavior and recycling process of Fe- Si- B amorphous ribbon[J]. , 2019, 31(1): 49-55. |
[4] |
WANG Chang,,YU Yang,,WANG Lin,,GUO Zi- feng,,L Bao- feng,WU Nai. Influence of chemical composition on surface quality of thin hot rolled pickled sheet[J]. , 2019, 31(1): 83-88. |
[5] |
HU Man,,MA Hui- ping,,JU Quan,,ZHANG Yong- lu,,DU Jin- hui,. Effect of silicon on oxidation behavior of GH3230 alloy[J]. , 2018, 30(4): 334-339. |
[6] |
WANG Bin,YE Dong- dong,CHEN Jian- jun,SUN Quan,AN Qi. Experimental and numerical analysis of compression fracture for strip steel oxidation film[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 762-767. |
|
|
|
|