Evolution of Cold Rolling and Annealing Textures in Nonoriented Electrical Steel |
JIN Zili,REN Huiping,WANG Yufeng,XU Xiangqi |
Institute for Materials and Metallurgy, Inner Mongolia University of Science and Technology, Baotou 014010, Inner Mongolia, China |
|
|
Abstract An overall study of hot rolling texture and the evolution of cold rolling and recrystallization textures in 50W600 electrical steels were conducted by orientation distribution function analysis and experiments on cold rolling and annealing. Results show that the hot band presents almost random texture and the intensity of αfibre texture is weak. With increasing cold rolling deformation rate the intensity of αfibre texture is increased, the intensity of {001}<110> and {112}<110> are 12 and 14 respectively at the cold reduction rate of 81%. With increasing annealing temperature and holding time the intensity of αfibre texture is weakened and the intensity of {001}<110> and {112}<110> is greatly decreased but the {111}<112> of γ fibre texture is significantly increased,presenting that most of grains are oriented along γfibre texture. It’s favorable to develop the cold rolled nonoriented electrical steels with strong {100} texture by controlling the parameters of cold rolling and annealing.
|
Received: 01 January 1900
|
|
|
|
[1] |
QIAN Cheng, ZHANG Jia-sheng, BAI Zhen-hua, CUI Ya-ya, HUA Chang-chun, CHEN Shu-zong. Oil film thickness model of roll surface and its influencing factors during double cold rolling[J]. Iron and Steel, 2020, 55(6): 68-74. |
[2] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
[3] |
WANG Lin, SHEN Jie. Application of laser-induced breakdown spectroscopy technology on analysis of surface inclusions of cold rolled plate[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 37-. |
[4] |
BAI Zhen-hua, CUI Ya-ya, LI Xiu-jun, XIA Yi-wei. Development of emulsion pipeline direct mixed lubrication system in double cold reduction mill[J]. Iron and Steel, 2020, 55(1): 56-64. |
[5] |
LI Xiujun1,2,CUI Yaya1,3,BAI Zhenhua1,4. Online control technology of emulsion volume percent in double cold reduction mill[J]. Iron and Steel, 2019, 54(9): 79-84. |
[6] |
GAO Xiangming1,PEI Mingde1,2,LI Guoping1,2. Influence of cold rolling on precipitation of S32750 super duplex stainless steel[J]. Iron and Steel, 2019, 54(9): 94-98. |
|
|
|
|