Influence of Aluminum content on the Texture and Performance of GCr15 Draw Steel |
Hu Wen-Hao |
|
|
|
Abstract This paper deals with the impact of different aluminum content in annealed GCr15 draw steel on the variation of strip texture, microstructure, gain orientation, hardenability n-value, plastic strain ratio r-value and Δr index under the condition of mass production in Hangzhou Iron & Steel Group Co. Experimental results show that within the range of [Al] s=0.017~0.027%, the influence of aluminum on the property of deep-drawing formed GCr15 with high carbon and with low carbon is basically the same. With the increase of aluminum content, the r-value is increased, while the beneficial texture on {111} also go up. However, the r- value of GCr15 steel is much less than that in the low-carbon steel with the same degree of aluminum. While n-value remains more or less the same, Δr index is much smaller, and there is some significant difference in grain orientation. All of these indicate that GCr15 with high carbon has good properties in the above-mentioned aspect, which can meet the requirements of deep forming for common purposes.
|
Received: 15 June 2009
|
|
|
|
[1] |
LI Zhao-zhen, SONG Xin-li, LIU Jing, CHENG Zhao-yang, BI Yun-jie, JIA Juan. Effect of Cr,Mn and annealing temperature on properties of non-oriented silicon steel[J]. Iron and Steel, 2020, 55(5): 80-86. |
[2] |
CAI Zhen, LIANG Wen, WANG Shui-ze, LIU Yong-qian. Discussion about practice and process of ferrite rolling in Ti-IF steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 7-. |
[3] |
ZHOU Liu-tao, PAN Hong-bo, PAN Shuo, WU Jie-wen. Effect of annealing process on microstructure texture and mechanical properties of 0.025C-0.326Mn steel[J]. Iron and Steel, 2020, 55(1): 93-100. |
[4] |
ZHANG Jian-jun,KOU Sha-sha,LI Wen-ya. CauseanalysisofDC06deepdrawingcrack[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(5): 47-50. |
[5] |
LI Cheng- gang,ZHANG Yuan- xiang,WANG Yang,FANG Feng,CAO Guang- ming. Study on secondary recrystallization of Goss grains in strip- cast grain- oriented electrical steels[J]. , 2019, 31(2): 202-206. |
[6] |
CHENG Si- fei,JIAO Hai- tao,XU Yun- bo. Microstructure evolution during deformation and heat treatment of strip- cast oriented Fe- 6. 5%Si steel[J]. , 2019, 31(2): 233-238. |
|
|
|
|