Local Brittleness of HeatAffected Zone of X80 Pipeline Steel |
ZHANG Xiaoli1,2,ZHUANG Chuanjing1,FENG Yaorong1, ZHAO Wenzhen2,HUO Chunyong1 |
1. Research Institute of Tubular Goods, CNPC, Xi’an 710065, Shanxi, China;2. School of Material Science and Engineering, Xi’an Jiaotong University, Xi’an 710049, Shanxi, China |
|
|
Abstract Impact Charpy toughness and local brittleness of HAZ of X80 linepipes made in China were studied. It was shown that the impact toughness of HAZ is 50% of base metal.From 20 ℃ to -40 ℃, the fracture is changed from part brittleness to total brittleness.At 20 ℃,the radial region is a mixture of cavitation and cleavage fracture and at 20 ℃and 0 ℃ the microcracks could be observed in radial region and fibrous region, respectively.The microstructure of fracture surface of HAZ is of granular bainite,with characteristics of coarse crystal zone.The propagation of microcracks goes along grain boundaries, the size of M/A islands in granular bainite is increased, and the phenomenon of crack traversing through M/A island exists as the result of serious embrittlement of grain boundary in HAZ.
|
Received: 01 January 1900
|
|
|
|
[1] |
SHAO Chun-juan,ZHEN Fan,ZHANG Ji-ming,QU Jin-bo,ZHANG Lei. Effect of sample thinning on DWTT property of heavy wall X80 steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 497-504. |
[2] |
CHEN Ming-xin1,YANG Xiao-jiang2,MENG Qing-yong2. Study on high temperature thermoplasticity of medium manganese steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 519-524. |
[3] |
SUN Ming-han, ZHU Zhi-wang, ZHENG Li-kang, ZHENG Chuan-xing, DU Feng-shan. Mechanism of oblique edge crack formation of cast-rolling strip[J]. Iron and Steel, 2020, 55(4): 60-67. |
[4] |
Danny Wei. [J]. , 2020, 45(3): 0-0. |
[5] |
XING Xian-qiang, CAO Wen-quan, WANG Cun-yu. Bond structure of 55SiCr steel used for coil springs of automotive suspension system[J]. Iron and Steel, 2020, 55(3): 68-73. |
[6] |
ZHOU Ren-yuan, ZHU Li-hui, LI Shi-xian, ZHAI Guo-li. Improvement of reheat-cracking susceptibility and microstructure of T23 steel[J]. Iron and Steel, 2020, 55(3): 80-86. |
|
|
|
|