Influencing Factors on High Temperature Properties of Iron Ore in Shougang |
ZHAO Zhi-Xing |
|
|
Abstract The high temperature properties of iron ore, such as assimilation, liquid phase fluidity, can reflect behaviours at high temperature during sintering, compared with the normal temperature properties of iron ore, so the high temperature properties of iron ore are significant for optimizing ore sintering matching. In this paper, high temperature properties of ores used in Shougang since 2000 were measured, compared and analysed, with results showing that combined water of ore promotes the assimilation of ore, and ore with high SiO2 content has high liquid phase fluidity under the same bascity, on the condition that CaO addition is no more than CaO amount according to eutectic temperature in CaO-Fe2O3.
|
Received: 26 February 2010
|
|
|
|
[1] |
DU Liang, HAN Xiu-li, ZHANG Quan-sheng, ZHOU Xiang, YANG Hong-da, WANG Ying. Quantitative relation between mineralogical structure and metallurgical properties of sinter of import iron ore[J]. Iron and Steel, 2020, 55(6): 38-45. |
[2] |
ZHU De-qing1,TIAN Hong-yu1,PAN Jian1,LIAO Hui2,GUO Zheng-qi1,XUE Yu-xiao1. Comprehensive utilization status and progress of low-grade laterite nickel ore[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 351-362. |
[3] |
ZHOU Ming-shun, WANG Yi-dong, ZHAO Dong-ming, HAN Hong-liang,LI Xian-chun, LU Li-ming. Development on sintering technologies with high proportion of magnetite concentrates[J]. Iron and Steel, 2020, 55(5): 1-9. |
[4] |
HE Zhan-wei, XUE Xiang-xin. Basic sintering characteristics of several typical vanadium titanium magnetite[J]. Iron and Steel, 2020, 55(5): 20-25. |
[5] |
ZHANG Wei-li, WU Sheng-li, HU Zhong-jie. Analysis of affecting factors of activated coke denitrationefficiency for sintering flue gas[J]. Iron and Steel, 2020, 55(5): 109-115. |
[6] |
ZHANG Wei-li1,WU Sheng-li1,HU Zhong-jie1,2. Statistical analysis of factors affecting desulfurization rate of activated coke for sintering flue gas[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 281-288. |
|
|
|
|