| Effect of Composition of an Econimical HotRolled TRIP Steel on Microstructure and Properties |
| ZHENG Fang1，2，ZHENG Lei2，WANG Guodong1 |
| 1. State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China;2. R & D Center, Baoshan Iron & Steel Co. Ltd., Shanghai 201900, China |
|
|
|
|
Abstract In order to utilize resource effectively and decrease the production cost, more attention is put on the economical high strength hot rolled TRIP(Transformation Induced Plasticity) steel.A hot rolled TRIP steel without any expensive alloying element was developed.The hot rolled TRIP steel sheets 3.0 mm in thickness were produced on a pilot mill with controlled rolling and stepped cooling from the ingot cast in a vacuum induction furnace in laboratory. The effect of carbon, silicon and manganese on the microstructure and properties were studied by tensile test and microstructure analysis. The results show that the tensile strength of the steel increases with increasing carbon or manganese content, but the elongation of the steel decreases with carbon content increasing. The increase of silicon content increases the strength and does not affect the elongation. In this case, the product of tensile strength and elongation (TS×T.EL) increases. 600 MPa high strength hotrolled TRIP steel with TS×T.EL of 21833 MPa·% and 800 MPa high strength hotrolled TRIP steel with TS×T.EL of 24650 MPa·% can be produced by controlling the content of carbon, silicon and manganese and rolling process.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
TIAN Ya-qiang1,BI Wen-qiang1,PAN Hong-bo2,LI Hong-bin1,ZHENG Xiao-ping1,CHEN Lian-sheng1. Effect of carbide evolution on Lüders behavior of cold rolled ART 0.1C-7Mn steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 505-511. |
| [2] |
ZHAO Yun-peng, YU Chao, XIAO Hong, WU Zong-he, XU Peng-peng, XIE Hong-biao. Effect of pure iron interlayer on mechanical properties of hot rolled stainless steel clad plate[J]. Iron and Steel, 2020, 55(5): 73-79. |
| [3] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
| [4] |
CAI Zhen， LIANG Wen， WANG Shui-ze， LIU Yong-qian. Discussion about practice and process of ferrite rolling in Ti-IF steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 7-. |
| [5] |
ZHOU Cong-rui， CHEN Xiao-long， ZHOU Ming-ke，FAN Lei， MEI Peng， BAO Si-qian. Cause analysis of surface blackening of SPHC hot rolled strip after pickling[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 41-. |
| [6] |
SUN Ming-han, ZHENG Yi, QU Chun-tao, JIN Shi-zhe, XU Zhi-qiang, DU Feng-shan. Numerical simulation of temperature field in ultra-fast cooling process of hot rolled plate[J]. Iron and Steel, 2020, 55(3): 50-57. |
|
|
|
|
2007, Vol. 42 