Shape Control With Varying Contact Backup Rolls on Tandem Cold Rolling Mill |
LU Haitao1, CAO Jianguo1, ZHANG Jie1, JIA Shenghui2, ZENG Wei2 |
1. School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China;2. Wuhan Iron and Steel (Group) Corp., Wuhan 430083, Hubei, China |
|
|
Abstract The configuration of conventional backup and work rolls for revamped 1700 tandem cold rolling mill at WISCO was proved unreasonable by systematical test as the cause of work roll edges contact during thin strip rolling and unsatisfactory flatness of product. A 2dimensional varying thickness finite element model of roll system deformation was built to simulate and analyse rolling process, and then a VCR (varying contact backup roll) was designed for the rolling conditions of PLTCM (pickling line combined with tandem cold rolling mill) and has been applied to 1700 tandem cold rolling mill at WISCO after industrial test. The application of VCR improves shape control,giving better strip flatness, higher capacity for thin strip and better selfmaintenance of roll contours.
|
Received: 01 January 1900
|
|
|
|
[1] |
QIN Da-wei, LIU Hong-min, ZHANG Dong, WANG Jun-sheng. Prediction models of coating mass per unit area for hot-dip galvanized strip based on artificial neural network[J]. Iron and Steel, 2020, 55(5): 68-72. |
[2] |
ZHOU Cong-rui, CHEN Xiao-long, ZHOU Ming-ke,FAN Lei, MEI Peng, BAO Si-qian. Cause analysis of surface blackening of SPHC hot rolled strip after pickling[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 41-. |
[3] |
XIAO Hong, XU Zi-an, ZHANG Chun-jie. Incremental solution of internal stress in coiling process of cold rolled strip[J]. Iron and Steel, 2020, 55(2): 82-87. |
[4] |
ZHAO Ding-cheng,MA Shu-mei. Influence of electromagnetic screen on temperature uniformity of strip steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(1): 1-. |
[5] |
MA Wei1,LI Wei-gang1,2,ZHAO Yun-tao1,YAN Bao-kang1. Prediction of hot-rolled roll force based on deep learning[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(9): 805-815. |
[6] |
YANG Geng-wei,LU Jia-wei,SUN Hui,FANG Zi-wei,ZHOU Yi-liao,YAO Nan. Microstructure, mechanical properties and phase transformation behavior of TiV microalloyed highstrength hotstrip steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 726-732. |
|
|
|
|