| ELC Steel Production by Ferritic Hot Rolling Process |
| zhaodong wang |
| |
|
|
|
|
Abstract The hot rolled microstructure, texture and properties of an ELC steel hot rolled in ferrite region, cold rolled and annealed were studied. The results show that deformation bands are the main microstructure in the hot rolled sample and fish-bone in-grain shear bands are visible when magnification times is 1000. Texture is homogenous along the thickness direction of the sheet in hot rolled, cold rolled as well as annealed status. r-value of the cold rolled and annealed sheet is around 1.3, meeting the needs of DQ class.
|
|
Received: 28 August 2008
|
|
|
|
| [1] |
LI Zhao-zhen, SONG Xin-li, LIU Jing, CHENG Zhao-yang, BI Yun-jie, JIA Juan. Effect of Cr,Mn and annealing temperature on properties of non-oriented silicon steel[J]. Iron and Steel, 2020, 55(5): 80-86. |
| [2] |
CAI Zhen， LIANG Wen， WANG Shui-ze， LIU Yong-qian. Discussion about practice and process of ferrite rolling in Ti-IF steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 7-. |
| [3] |
ZHOU Liu-tao, PAN Hong-bo, PAN Shuo, WU Jie-wen. Effect of annealing process on microstructure texture and mechanical properties of 0.025C-0.326Mn steel[J]. Iron and Steel, 2020, 55(1): 93-100. |
| [4] |
SUN Zhi-peng， XU Yan， SONG Zu-feng. Concrete manifestation and cause analysis of the abnormal r-value of the tensile testing machine[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(1): 24-. |
| [5] |
XU Yan， SUN Zhi-peng， SONG Zu-feng. Elimination of r-value anomaly of width extensometer by linear fitting method[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(1): 28-. |
| [6] |
ZHANG Jian-jun，KOU Sha-sha，LI Wen-ya. CauseanalysisofDC06deepdrawingcrack[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(5): 47-50. |
|
|
|
|
2009, Vol. 1 