Process Control of Dephosphorization by MultiFunctional Refining in Converter |
LAI Zhaoyi1,2,XIE Zhi1 |
1. School of Information Science and Engineering, Northeastern University, Shenyang, 110004, Liaoning, China;2. Steelmaking Plant, Fujian Sansteel, Sanming 365000, Fujian, China |
|
|
Abstract The porblems caused by low hot metal ratio and low dephosphorization rate was solved by multifunctional refining in converter at Fujian Sansteel.Based on thermodynamics and experiments, the temperature range for dephosphorization was obtained. The factors influencing on dephosphorization were analyzed and suitable slag basicity and (FeO) content in molten slag were determined. The results show such refining makes the end phosphorus content to meet the requirements for high quality steel,and product cost can be reduced.
|
Received: 01 January 1900
|
|
|
|
[1] |
WANG Kun1,LIU Xiao-jie1,LIU Er-hao2,LI Hong-yang1,LIU Song1,LV Qing1. Core temperature prediction model based on AdaBoost algorithm[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 363-369. |
[2] |
YANG Li-bin, ZENG Jia-qing, DENG Yong, XU Xiao-wei, WU Li-ping. Highly efficiency and long-life combined blowing technology of big converter[J]. Iron and Steel, 2020, 55(4): 45-52. |
[3] |
SI-Jun LI du jinjinke. Numerical Simulation Study on Single-point Unequilibrium Casting for Beam Blank in Laiwu Iron and Steel Company[J]. , 2020, 45(3): 0-0. |
[4] |
ZHAO Dong,ZHANG Jing,LUO Guo-ping,CHEN Yan-biao,ZHANG Xiang. Effect of SiO2 and Na2CO3 addition on gasification dephosphorization during prereduction and sintering of iron concentrate[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(3): 204-211. |
[5] |
WANG Xiao-lei1,SHI Xue-feng1,HU Chang-qing1,WANG Xin-dong2,HU Qi-chen2. Experimental study on spherication and cold performance of highsilica magnesium flux pellets[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(3): 212-219. |
[6] |
WANG Fei,HOU Shao-lin,ZHAO Chang-shun,LI Ru,BAI Ming-xi. Effect of austenitizing temperature on strength-toughness of high strength steel 15Cr2MnNi2TiA[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(2): 9-. |
|
|
|
|