Effect of Solution Treatment on Mechanical Properties of a New Maraging Stainless Steel |
LIU Zhenbao1,YANG Zhiyong1,YONG Qilong1,LIANG Jianxiong1,LUlun2 |
1. Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081, China; 2. Technical Center, Dongbei Special Steel Group, Fushun 113001, Liaoning, China |
|
|
Abstract The effect of solution treatment on mechanical properties of a new stainless steel, CrNiCoMo maraging stainless steel was studied. The result shows that there are intermetallics in the steel solution treated at a temperature lower than 1050 ℃ with χ phase as the major phase. The intermetallics deteriorate toughness of the steel,and the strength of the steel is reduced by 100 MPa. There is lathy martensite of high density dislocation in the steel after 1050 ℃ solid solution treatment for one hour. By proper aging treatment, the strength of the steel may reach up to 1940 MPa,with a good combination of strength and toughness.
|
Received: 01 January 1900
|
|
|
|
[1] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
[2] |
ZHAO Yun-peng, YU Chao, XIAO Hong, WU Zong-he, XU Peng-peng, XIE Hong-biao. Effect of pure iron interlayer on mechanical properties of hot rolled stainless steel clad plate[J]. Iron and Steel, 2020, 55(5): 73-79. |
[3] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
[4] |
XING Xian-qiang, CAO Wen-quan, WANG Cun-yu. Bond structure of 55SiCr steel used for coil springs of automotive suspension system[J]. Iron and Steel, 2020, 55(3): 68-73. |
[5] |
YANG Chen-xing1,2,WU Zhi-wei1,2,YANG Mao-sheng2,ZHAO Kun-yu1. Microstructure and mechanical properties of Ni-Cr bearing alloy in solution aging treatment[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(3): 242-252. |
[6] |
WANG Ji-hong, ZHANG Li-na, CHEN De-li, QI Yue, CAO Li-hong. Discussion about heat treatment process of X20Cr13 blade steel for gas turbine[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 18-. |
|
|
|
|