| Research on Hot Metal Dephosphorizing Pretreatment and Direct Steel-making Process in 100t converter |
| |
|
|
|
|
Abstract The present paper introduces the practice of improving the end point target-hitting by adoption of hot metal dephosphorizing pretreatment and direct steel-making process in 100t converter. Cold smelting charge ratio was respectively 20%,25%,28%, by optimizing slag making and oxygen blowing process of dephosphorizing pretreatment period and decarburizing period，oxygen consumption rate increased from 20～30% to 40～50% than conventional process in dephosphorizing pretreatment period and slag charge was controlled at 8～15kg.t-1 in decarburizing pretreatment period. Fifty heats industrial test results indicated that temperature controlling at first slag off achieve the level of conventional smelting process, the controlling levels of [C] and [P] were significantly better than conventional smelting process.
|
|
Received: 13 March 2009
|
|
|
|
| [1] |
LI Lin, LI Ming-ming, LI Qiang, ZOU Zong-shu. Melt splashing behavior of steelmaking converter with nozzle-twisted lance[J]. Iron and Steel, 2020, 55(6): 54-60. |
| [2] |
YANG Li-bin, ZENG Jia-qing, DENG Yong, XU Xiao-wei, WU Li-ping. Highly efficiency and long-life combined blowing technology of big converter[J]. Iron and Steel, 2020, 55(4): 45-52. |
| [3] |
DONG Wen-liang, PAN Hong-wei, LUO Lei, JI Chen-xi, LI Hai-bo, TIAN Zhi-hong. Phosphorous distribution in dephosphorization slag[J]. Iron and Steel, 2020, 55(2): 75-81. |
| [4] |
ZHOU Zhenyu, TANG Ping, ZHOU Zunchuan, HOU Zibing, WEN Guanghua. Optimization on nozzle parameters of 200 t combined blowing vanadium extraction converter[J]. Iron and Steel, 2019, 54(9): 50-56. |
| [5] |
WANG Linzhu，BAO Yanping，LI Xiang. Comparison of twostage dephosphorization during remaining #br# slagdouble slag process in converter[J]. Iron and Steel, 2019, 54(8): 37-42. |
| [6] |
HUANG Bing,ZHU Ming-mei,ZHONG Yong,ZHANG Ai-ping,WANG Yu. Thermodynamic calculation of phase composition of CaOSiO2FeOCr2O3MgOMnO slag system[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 718-725. |
|
|
|
|
2010, Vol. 45 