Reason and Control Practice of Hearth Sidewall Erosion of No.2 BF at Baosteel |
XU Wanren1,ZHU Renliang2,ZHANG Longlai2,ZHANG Yongzhong2 |
1. Technology Center of Baoshan Iron and Steel Co., Ltd., Shanghai 201900, China; 2. Ironmaking Plant of Baosteel Branch, Baoshan Iron and Steel Co., Ltd., Shanghai 200941, China |
|
|
Abstract The reasons of temperature rise of hearth sidewall for several times were analyzed and the operation practice on control of sidewall erosion was summarized for No.2 BF at Baosteel. Results indicate that the sharp circumferential flow of hot metal and slag is the major factor of intensified hearth sidewall erosion. By the measures in operation such as activation of hearth deadman, enhancement of central gas flow, rise of hearth bottom temperature as well as improvement of taphole protection, the problem of hearth wall erosion on No.2 BF was solved successfully. Meanwhile, the effect of adding titanium ore on hearth bottom maintenance is notable, but not obvious for the control of hearth sidewall erosion.
|
Received: 01 January 1900
|
|
|
|
[1] |
YAN Xue-qiang1,2,ZHENG Wan1,2,WANG Guo-wei1,2,YAN Wen1,LI Guang-qiang1,2. Effect of microporous MgO refractories on steel cleanliness[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 483-490. |
[2] |
LIU Lan-xiao, WANG Lin, WU Nai, ZHOU Na, WANG Lun, XU Ke-hao. Cause analysis and improvement measures of white line defect on tinplate surface[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(1): 41-. |
[3] |
MA Hengbao,JIAO Kexin,ZHANG Jianliang,FAN Xiaoyue,CHEN Yanbo,ZHENG Pengchao. Phase composition and properties analysis of slag crust in #br# largesize blast furnace copper stave[J]. Iron and Steel, 2019, 54(6): 20-26. |
[4] |
LIU Wen-hua,XU Gang-jun,ZHANG Li-qin. Causes and control measures of corner crack in DC01EK[J]. , 2019, 44(1): 49-53. |
[5] |
XIANG Zhong-yong,JIANG Xi,. Analysis of production indexes of large BF by new evaluation method for production efficiency[J]. Iron and Steel, 2018, 53(8): 38-43. |
[6] |
ZHANG Zheng-lin, WANG Xiang-hong. Control of longitudinal surface crack of tube steel A29[J]. , 2018, 43(6): 71-73. |
|
|
|
|