Distribution Behaviors of Vanadium Between Hot Metal and FeO-SiO2-MnO Slag System |
DONG Jin-ming1,2,ZHAO Fei3,ZHANG Yan-ling3,QIU Sheng-tao1,GAN Yong1 |
|
|
Abstract Under laboratory conditions, the distribution behavior of vanadium between hot metal and slag system of FeO-SiO2-MnO slag at 1380℃ was studied. The results show:the extraction rate of vanadium from the hot metal, the distribution ratio of vanadium between slag and metal phases, and vanadium capacity of slag decrease with increasing SiO2 content;the parameters mentioned above increase with increasing MnO content in the condition of keeping SiO2 content at lower level, when the SiO2 content is larger than 20% they firstly increase and then decrease with increasing MnO content;in the slag system of FeO-SiO2-MnO, they reach the maximum value in the region of keeping w(SiO2) at 10%-20% and w(MnO) at 13%-25%, which is corresponding to the region of giving the lowest melting point; the magnitude of the activity coefficient of V2O3 in FeO-SiO2-MnO slag system is 10-6-10-7.
|
Received: 14 September 2010
Published: 25 July 2011
|
|
|
|
[1] |
CHENG Xiang-kui, ZHAO Ying-tao, ZHAO Xu, WANG Jun, HUANG Xiao-li, PU Chun-lei. Preparation of V-Ti magnetite ore basic pellet containing NaOH[J]. Iron and Steel, 2020, 55(6): 33-37. |
[2] |
MA Li-ming,ZHANG Jian-liang,WU Sheng-li,LIU Zheng-jian,WANG Yao-zu,XU Chen-yang. Treatment of vanadiumtitanium magnetite based on fluxed green ball composite agglomeration process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 462-469. |
[3] |
HE Zhan-wei, XUE Xiang-xin. Basic sintering characteristics of several typical vanadium titanium magnetite[J]. Iron and Steel, 2020, 55(5): 20-25. |
[4] |
ZHOU Zhenyu, TANG Ping, ZHOU Zunchuan, HOU Zibing, WEN Guanghua. Optimization on nozzle parameters of 200 t combined blowing vanadium extraction converter[J]. Iron and Steel, 2019, 54(9): 50-56. |
[5] |
HUANG Bing,ZHU Ming-mei,ZHONG Yong,ZHANG Ai-ping,WANG Yu. Thermodynamic calculation of phase composition of CaOSiO2FeOCr2O3MgOMnO slag system[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 718-725. |
[6] |
. Analysis of Skin Warping Defect of High Strength Steel Strengthened by Ferric Vanadium Nitride[J]. , 2019, 44(6): 0-0. |
|
|
|
|