Analysis of Flange Crack on Hot-Rolled H Section Steel of SS400 |
WANG Ke-feng1,SONG Jie-zhong2,LI Ming-xian1,HE Li-guo1,ZHAO Rui2 |
1. Quality Division, Rizhao Steel Co., Ltd., Rizhao 276806, Shandong, China 2. Technology Center, Rizhao Steel Co., Ltd., Rizhao 276806, Shandong, China |
|
|
Abstract Based on 842 heats of SS400, the flange crack of hot-rolled H section steel of SS400 was analyzed by using optical microscope, scanning electron microscopy and other methods .The results indicated that the blister, edge crack, surface inclusion and skin blowhole are the main factors causing the flange crack defect. The measures for improving H section steel quality were put forward such as controlling chemical compositions and stirring time, increasing the ratio of manganese and sulphur, decreasing inclusions and ensuring adequate tundish baking time, reforming the mould powder, decreasing overheat of tundish, adjusting the process parameters and optimizing the secondary cooling.
|
Received: 02 December 2010
Published: 09 October 2011
|
|
|
|
[1] |
DENG Aijun,PU Xuefeng,ZUO Xiaotan,FAN Dingdong,ZHENG Anmin. Study and optimization of Vnotch cracking in Hbeam[J]. Iron and Steel, 2019, 54(8): 161-167. |
[2] |
. Causes and countermeasures of subsurface bubbles of the boron steel[J]. , 2019, 44(2): 0-0. |
[3] |
CAI Zhao- zhen,AN Jia- zhi,LIU Zhi- yuan,NIU Zhen- yu,ZHU Miao- yong. Research on development and application of micro- alloyed steel slab corner transversal crack control technology[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(2): 117-124. |
[4] |
SU Rui-xian,SU Zhi-jian. Process optimization of high carbon tool steel slab continuous casting[J]. , 2019, 44(1): 18-21. |
[5] |
XU Dao-song,YE Sheng-yuan,HUANG Jian,ZHOU Min-jie. Cracking cause analysis of elevator rail[J]. , 2018, 36(3): 35-38. |
[6] |
YE Yu-kui,GUI Zhong-lin,WANG Xiang-hong. Optimization practice of corner radius of billet mold[J]. , 2018, 43(1): 25-28. |
|
|
|
|