Thermodynamic Calculation and Experimental Measurement of δ-Ferrite Amount in P92 Heat-Resistant Steel |
SHI Ru-xing,LIU Zheng-dong,ZHANG Cai-ming |
Institute for Structural Materials, Central Iron and Steel Research Institute, Beijing 100081, China |
|
|
Abstract The effect of processing temperature on δ-ferrite amount in P92 steel was experimentally investigated. Results show that the amount of δ-ferrite decreases firstly and then increases after approaching its lower peak around 1050℃, within the temperature scope from 900℃ to 1200℃. With the help of the Thermo-Calc software, the pseudo-equilibrium phase diagrams of P92 steel were calculated. Its prediction on δ-ferrite evolution agrees well with aforementioned measurement. These pseudo-equilibrium phase diagrams can reasonably explain the experimental results.
|
Received: 25 August 2010
Published: 17 November 2011
|
|
|
|
[1] |
ZHAO Zhong-yu, ZHAO Jun-xue, TAN Ze-xin, LU Liang, CUI Ya-ru, LI Xiao-ming. Determination and analysis of CaF2-Al2O3 binary phase diagram based on volatilization effect[J]. Iron and Steel, 2020, 55(4): 34-39. |
[2] |
WANG Xiao-ai1, JIANG Xin2, GAO Yuan3, HUO Hong-yan3, SHEN Feng-man2. Investigation on fluidity of SFCA and sintering strength based on phase diagram[J]. Iron and Steel, 2019, 54(5): 9-13. |
[3] |
LIN Teng- chang,ZHU Rong,ZENG Jia- qing. Thermodynamic simulation of slag- steel O- equilibrium based on 20CrMnTi refining composition[J]. Chinese Journal of Iron and Steel, 2016, 28(3): 48-50. |
[4] |
ZHAI Guo-li, WANG Qi-jiang. Effect of Cr content on microstructure and property of P92 steel[J]. Iron and Steel, 2016, 51(11): 68-72. |
[5] |
LIU Dong-hui, ZHAO Ya-juan, LI Ping-he. Discussion on abnormal microstructure of offshore platform steel E550[J]. Chinese Journal of Iron and Steel, 2015, 33(2): 48-51. |
[6] |
YANG Jun, DU Jiang, CHEN Bo-tao, WU Jun-xiong. Influence of calcium treatment on oxide inclusions in ultra-low oxygen refining process[J]. Iron and Steel, 2015, 50(1): 19-26. |
|
|
|
|