| Effects of Tempering Temperature on Microstructure and Mechanical Properties for Q960 High-strength Structural Steel Plates |
| LU Feng1,2,KANG Jian1,WANG Chao1,WANG Zhao-dong1,WANG Guo-dong1 |
1. State Key Lab of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China
2. Wide Heavy Plate Project Manager Department of Tangshan Iron and Steel Corporation, Tangshan 063000, Hebei, China |
|
|
|
|
Abstract To develop the Q960 high-strength quenched and tempered structural steel plates, the effects of tempering temperature on the microstructure and mechanical properties of plate specimens were investigated on the same rolling and quenching conditions. The results show that with the increase of tempering temperature, the strength values of specimens are reduced, and the toughness and ductility show a mainly increasing tendency. But the temper brittleness appears at 300~450℃. The excellent overall properties of specimens with tempered sorbite can be obtained when the tempering temperature is 600℃, i.e., the yield strength is 1030MPa, tensile strength 1080MPa and percentage elongation 15.9% with the Charpy impact energy 144J at -40℃. All these indexes come up to the National Standard GB/T 16270-2009. Then the tensile behavior of specimens was discussed.
|
|
Received: 04 November 2010
Published: 20 February 2012
|
|
|
|
| [1] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
| [2] |
JIANG Yue-yue, WANG Zhao-dong, DENG Xiang-tao. Effect of trace rare earth Ce on martensitic transformation behavior of ultra-high strength low alloy steel[J]. Iron and Steel, 2020, 55(6): 84-90. |
| [3] |
YANG Guang-feng,LU Meng-ke,ZHANG Hang,ZHAI Wei,CUI Jing. Corrosion behavior and mechanism of 300M ultra high strength steel in neutral salt spray environment[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 406-415. |
| [4] |
ZHAO Yun-peng, YU Chao, XIAO Hong, WU Zong-he, XU Peng-peng, XIE Hong-biao. Effect of pure iron interlayer on mechanical properties of hot rolled stainless steel clad plate[J]. Iron and Steel, 2020, 55(5): 73-79. |
| [5] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
| [6] |
CAO Jing-hua1,PAN Hong-bo2,3,ZHANG Jing1,ZHANG Teng-fei2,LI Xu-dong2,LIU Wei-ming2,3. Continuous cooling transformation of NbTi microcarbon deep drawing dualphase steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 322-328. |
|
|
|
|
2012, Vol. 47 