Effect of Forging Ratio on Microstructure and Mechanical Property of H13 Steel |
PEI Yue-kai1,2,MA Dang-shen2,LIU Bao-shi3,CHEN Zai-zhi2,ZHOU Rong1,ZHOU Jian2 |
1. Institute of Materials and Metallurgy Engineering, Kunming University of Science and Technology, Kunming 650093, Yunnan,China.2. Institute for Structure Materials, Central Iron & Steel Research Institute, Beijing 100081, China.3. Technology Center of Dongbei special steel group co. ltd, Fushun 113001, Liaoning , China |
|
|
Abstract Effect of different forging ratios on microstructure and mechanical properties of electrical die steel (H13) was investigated by metallographic microscope and SEM under simplex stretching and hot-forging condition. The results show that transversal impact property is much less than longitudinal in the same forging ratio. Following the forging ratio increasing, it makes merely influence on the transversal impact property, while the longitudinal impact property increases. The research shows that, the cross direction crack arrest property won’t be effectively influenced by forging ratio under simplex stretching and hot-forging condition. The forging ratio of electrical hot die steel should be controlled in four to six, which is most appropriate.
|
Received: 22 December 2010
Published: 20 February 2012
|
|
|
|
[1] |
LI Dong-hui, XIAO Mao-guo, SUN Hao, HE Wen-chao, ZHANG Xu, LI Shao-hong. Effects of deep cryogenic treatment on microstructure and thermal stability of H13 steel[J]. Iron and Steel, 2020, 55(2): 95-102. |
[2] |
GENG Hao, ZHANG Zhong-hua, TANG Hai-yan, LAN Peng, LUO Ming, ZHANG Jia-quan. Study on segregation and Nbbearing precipitates of highstrength oil well casing steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(4): 387-393. |
[3] |
WANG Xin-cheng,ZHANG Quan-xin,XU Hong-hao. Causes analysis of crack of 30CrNi3A pressplate[J]. , 2019, 37(1): 40-43. |
[4] |
HUANG Yu- bo,ZHANG Qi,WEN Yi- bei,SONG Zhao,ZHOU Ming- xing,XU Guang. Effects of Ni on microstructures and properties of high carbon nano- structured bainite steels[J]. , 2018, 30(9): 735-740. |
[5] |
XIAO Zhi- xia,,,LI Hai- peng,,,FENG Jian- hang,,,MI Yong- wang,NIE Yi- hong5,YIN Fu- xing,,. Microstructure homogeneity of high speed steel M2 ingot by electroslag remelting[J]. , 2018, 30(7): 529-535. |
[6] |
SUN Xiao-lin,,WANG Fei,,MAO Ming-tao,,CHEN Xi-chun,,DU Guang-wei,GUO Han-jie. Formation and affecting factors of V-rich primary carbides in H13 steel[J]. Iron and Steel, 2018, 53(5): 68-75. |
|
|
|
|