新型中锰马氏体高强度钢的耐磨性能

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (0 KB) HTML (0 KB)
Export: BibTeX | EndNote (RIS)

Abstract The abrasive wear behavior of new type medium manganese high strength martensite steels with 0.12% and 0.19% carbon content were determined by the pin-on-disc abrasion test and three-body impact abrasive test, and was contrasted with steels of Hardox450 and 21C. The wear properties of the specimens were evaluated by weight loss measurements. In order to evaluate the wear mechanism of different steels, the post-test characterization of the worn surfaces were performed using LOM, SEM and XRD. The results show that the wear resistance of new type medium manganese martensite steels is comparable with the wear resistant steels of Hardox450 and 21C. The wear weight lost of the studied steel tested both in pin-on-disc abrasion and three-body impact abrasion is approximately linearly proportional to its HV hardness, i.e., the higher the hardness, the better wear resistance of steels. Due to the addition of medium-Mn, the new typed steel assumes the advantages not only the Mn-solid strengthening to improve the wear resistance ability but its hardenability could be obtained at all cooling rate, which make the steel has the potential to be produced in steel industry.

Key words： wear resistance steel martensite high strength abrasive wear

Received: 02 September 2011 Published: 14 January 2013

PACS:

TG115

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	XUN Rong-Min

Cite this article:

XUN Rong-Min. Wear Resistant of New Type Medium Manganese High Strength Martensite Steel[J]. Iron and Steel, 2012, 47(12): 64-70.

URL:

http://www.chinamet.cn/Jweb_gt/EN/ OR http://www.chinamet.cn/Jweb_gt/EN/Y2012/V47/I12/64

[1]	Dastur Y.N，Leslie WC. Mechanism of work hardening in Hadfield manganese steel[J].. Metallurgical and Materials Transactions A,1981,12(5):749-
[1]	Dastur Y.N，Leslie WC. Mechanism of work hardening in Hadfield manganese steel[J].. Metallurgical and Materials Transactions A,1981,12(5):749-
[2]	Yan WL，Fang L，Sun K，Xu YH. Effect of surface work hardening on wear behavior of Had?eld steel[J]..[J].Mater Sci Eng A,2007,(460–461):542-
[2]	Yan WL，Fang L，Sun K，Xu YH. Effect of surface work hardening on wear behavior of Had?eld steel[J]..[J].Mater Sci Eng A,2007,(460–461):542-
[3]	王存宇，时捷.淬火-配分-回火工艺处理钢的三体冲击磨损性能研究[J].材料研究学报,2009,23(3):305-
[3]	王存宇，时捷.淬火-配分-回火工艺处理钢的三体冲击磨损性能研究[J].材料研究学报,2009,23(3):305-
[4]	曹艺.NM400高强度低合金耐磨钢的组织与性能[J].东北大学学报(自然科学版,2011,32(2):241-
[4]	曹艺.NM400高强度低合金耐磨钢的组织与性能[J].东北大学学报(自然科学版,2011,32(2):241-
[5]	王昭东，邓想涛. 新型低成本超高强低合金耐磨钢研究及其工业化应用[J]，钢铁，2010，45(8)：61
[5]	王昭东，邓想涛. 新型低成本超高强低合金耐磨钢研究及其工业化应用[J]，钢铁，2010，45(8)：61
[6]	José Rendón M O.Abrasive wear resistance of some commercial abrasion resistant steels evaluated by laboratory test methods[J].Wear,2009,267(11):2055-
[6]	José Rendón M O.Abrasive wear resistance of some commercial abrasion resistant steels evaluated by laboratory test methods[J].Wear,2009,267(11):2055-
[7]	Sundstr?m A，Rendon J，Olsson M.Wear behaviour of some low alloyed steels under combined impact/abrasion contact conditions[J].Wear,2001,250(1-12):744-
[7]	Sundstr?m A，Rendon J，Olsson M.Wear behaviour of some low alloyed steels under combined impact/abrasion contact conditions[J].Wear,2001,250(1-12):744-
[8]	中华人民共和国国家标准，工程机械用高强度耐磨钢板[S]，GB/T241862009
[9]	刘军刚.高强度耐磨钢板的生产现状及发展[J].莱钢科技,2010,146(2):1-
[8]	中华人民共和国国家标准，工程机械用高强度耐磨钢板[S]，GB/T241862009
[9]	刘军刚.高强度耐磨钢板的生产现状及发展[J].莱钢科技,2010,146(2):1-
[10]	Jie Shi，Wenquan Cao.Ultrafine Grained High Strength Low Alloy Steel With High Strength And High Ductility[J].Materials Science Forum,2010,654~656:238-
[10]	Jie Shi，Wenquan Cao.Ultrafine Grained High Strength Low Alloy Steel With High Strength And High Ductility[J].Materials Science Forum,2010,654~656:238-
[11]	Jie Shi，Wenquan Cao.Enhanced work-hardening behavior and mechanical properties in ultrafine-grained steels with large-fractioned metastable austenite[J].Scripta Materialia,2010,63(8):815-
[11]	Jie Shi，Wenquan Cao.Enhanced work-hardening behavior and mechanical properties in ultrafine-grained steels with large-fractioned metastable austenite[J].Scripta Materialia,2010,63(8):815-
[12]	Haiwen Luo，Jie Shi，Wenquan Cao.Experimental and numerical analysis on formation of stable austenite during the intercritical annealing of 5Mn steel[J].Acta materialia,2011,59(10):4002-
[12]	Haiwen Luo，Jie Shi，Wenquan Cao.Experimental and numerical analysis on formation of stable austenite during the intercritical annealing of 5Mn steel[J].Acta materialia,2011,59(10):4002-
[13]	Wenquan Cao.Microstructure and mechanical properties of Fe-02C-5Mn steel processed by ART-annealing[J].. Mater Sci Eng A,2011,528(22-23):6661-
[13]	Wenquan Cao.Microstructure and mechanical properties of Fe-02C-5Mn steel processed by ART-annealing[J].. Mater Sci Eng A,2011,528(22-23):6661-
[14]	Wenquan Cao，Jie Shi.The 3rd Generation Automobile Sheet Steels Presenting with Ultrahigh Strength and High Ductility[J].Advanced Steels,2011,3:209-
[15]	陈华辉，邢建东，李卫. 耐磨材料应用手册[M]. 北京：机械工业出版社，2006：39
[16]	章守华，吴承建. 钢铁材料学[M]. 北京：冶金工业出版社，1992：60
[14]	Wenquan Cao，Jie Shi.The 3rd Generation Automobile Sheet Steels Presenting with Ultrahigh Strength and High Ductility[J].Advanced Steels,2011,3:209-
[15]	陈华辉，邢建东，李卫. 耐磨材料应用手册[M]. 北京：机械工业出版社，2006：39
[16]	章守华，吴承建. 钢铁材料学[M]. 北京：冶金工业出版社，1992：60
[17]	Linlu Zhen，Yongxin Zhoul.An investigation of the abrasive wear behavior of ductile cast iron[J].Materials Processing Technology,2001,116(2-3):176-
[18]	饶启昌，桑可正.马氏体钢动载磨料磨损特性的研究[J].钢铁研究学报,1991,3(1):47-
[19]	崔忠圻. 金属学与热处理[M]. 北京：机械工业出版社，2000：183
[17]	Linlu Zhen，Yongxin Zhoul.An investigation of the abrasive wear behavior of ductile cast iron[J].Materials Processing Technology,2001,116(2-3):176-
[18]	饶启昌，桑可正.马氏体钢动载磨料磨损特性的研究[J].钢铁研究学报,1991,3(1):47-
[19]	崔忠圻. 金属学与热处理[M]. 北京：机械工业出版社，2000：183