Microstructures and Properties of a 600MPa High Strength Steel Under Ultra Fast Cooling Process |
YI Hai-long,XU Yang,SUN Ming-xue,LIU Zhen-yu |
The State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, Liaoning, China |
|
|
Abstract High strength steel with yield strength of 600MPa was investigated under ultra fast cooling process compared with laminar cooling process. An analysis was therefore made via testing for mechanical properties, SEM, TEM and EDS. The results show that the ultra fast cooling process can improve the performance of steel compared with the conventional laminar cooling process;the amount of yield and tensile strength are increased by 90MPa and 60MPa respectively; the yield strength, tensile strength and elongation are 670, 740MPa and 19%, and impact energy at -20℃ is 105J; good strength and toughness are obtained under ultra fast cooling process. The microstructure of steel under ultrafast cooling process is fine ferrite, and good strength is caused by the refinement of ferrite and precipitates.
|
Received: 19 April 2012
Published: 27 February 2013
|
|
|
|
|
[1] |
王国栋.新一代控制轧制和控制冷却技术与创新的热轧过程[J].东北大学学报:自然科学版,2009,30(7):913-922
|
[1] |
王国栋.新一代控制轧制和控制冷却技术与创新的热轧过程[J].东北大学学报:自然科学版,2009,30(7):913-922
|
[2] |
王国栋.新一代TMCP的实践和工业应用举例[J].上海金属,2008,30(3):1-4
|
[2] |
王国栋.新一代TMCP的实践和工业应用举例[J].上海金属,2008,30(3):1-4
|
[3] |
王国栋.以超快速冷却为核心的新一代TMCP技术[J].上海金属,2008,30(2):1-5
|
[3] |
王国栋.以超快速冷却为核心的新一代TMCP技术[J].上海金属,2008,30(2):1-5
|
[4] |
王新,陈小林,田士平,等..超快冷技术在首秦宽厚板生产线上的应用[J].钢铁研究学报,2011,S1:11-14
|
[4] |
王新,陈小林,田士平,等..超快冷技术在首秦宽厚板生产线上的应用[J].钢铁研究学报,2011,S1:11-14
|
[5] |
Yi H L,Xu Yang,Liu Z Y,et al.Influence of ultra-fast cooling technology on microstructure and mechanical properties of Ti-microalloyed steel[J].Advanced Materials Research,2011,337:414-417
|
[5] |
Yi H L,Xu Yang,Liu Z Y,et al.Influence of ultra-fast cooling technology on microstructure and mechanical properties of Ti-microalloyed steel[J].Advanced Materials Research,2011,337:414-417
|
[6] |
Li Fan,Yi H L,Liu Z Y,et al.Influence of cooling rate on the microstructures and properties of Q550[J].Applied Mechanics and Materials,2012,117-119:1705-1707
|
[6] |
Li Fan,Yi H L,Liu Z Y,et al.Influence of cooling rate on the microstructures and properties of Q550[J].Applied Mechanics and Materials,2012,117-119:1705-1707
|
[7] |
Herman J C,Donnay B,Leroy V.Precipitation kinetics of microalloying additions during hot-rolling of HSLA steels[J].ISIJ International,1992,32(6):779-785
|
[7] |
Herman J C,Donnay B,Leroy V.Precipitation kinetics of microalloying additions during hot-rolling of HSLA steels[J].ISIJ International,1992,32(6):779-785
|
[8] |
Misra R D K,Nathani H,Hartmann J E,et al.Microstructural evolution in a new 770MPa hot rolled Nb-Ti Microalloyed steel[J].Materials Science and Engineering A,2005,394(1-2):339-352
|
[8] |
Misra R D K,Nathani H,Hartmann J E,et al.Microstructural evolution in a new 770MPa hot rolled Nb-Ti Microalloyed steel[J].Materials Science and Engineering A,2005,394(1-2):339-352
|
[9] |
Charleux M,Poole W J,Militzer M,et al.Precipitation behavior and its effect on strengthening of an HSLA-Nb/Ti steel[J].Metallurgical and Materials Transactions A,2001,32(7):1635-1647
|
[9] |
Charleux M,Poole W J,Militzer M,et al.Precipitation behavior and its effect on strengthening of an HSLA-Nb/Ti steel[J].Metallurgical and Materials Transactions A,2001,32(7):1635-1647
|
[10] |
Cancio M J,Echaniz G,Perez T E.Characterisation of microalloy precipitates in the austenitic range of high strength low alloy steels[J].Steel Research,2002,73(8):340-345
|
[10] |
Cancio M J,Echaniz G,Perez T E.Characterisation of microalloy precipitates in the austenitic range of high strength low alloy steels[J].Steel Research,2002,73(8):340-345
|
[1] |
SUN Li-gen, LEI Ming, ZHANG Xin, LIU Yun-song, ZHU Li-guang. In-situ research on microstructure refining effect of Mg treatment for shipbuilding steel at high temperature[J]. Iron and Steel, 2020, 55(5): 94-102. |
[2] |
ZHU Li-guang, ZHENG Shi-wei, ZHANG Qing-jun, CAO Sheng-li. Influence of oxide metallurgy and pulsed magnetic field parameters on steel microstructure[J]. Iron and Steel, 2020, 55(3): 74-79. |
[3] |
DOU Wei-xue,WANG He-song,KANG Jian,LI Zhen-lei,YUAN Guo. Effect of cooling rate on microstructure of low-carbon steel produced by strip casting[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 748-753. |
[4] |
LOU Hao-nan,WANG Bing-xing,WANG Zhao-dong. Microstructure and properties of Ti-Mg oxide metallurgy steel under TMCP process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(12): 1039-1045. |
[5] |
CHENG Lin,HU Zhi-yuan,PANG Wei-guang,ZHAO Xiao-dong,LIU gong-tao,SHI Ai-chen. Inclusions distribution in non-oriented silicon steel and its influence on performance consistency of strip steel[J]. , 2019, 44(1): 44-48. |
[6] |
ZHAO Fu- cai,ZHANG Zhao- hui,YANG Lei,KE Jing. Development and prospect of calcium oxide metallurgical production technology[J]. , 2018, 30(4): 259-264. |
|
|
|
|