高磁感取向硅钢生产技术与工艺的研发进展及趋势

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (0 KB) HTML (0 KB)
Export: BibTeX | EndNote (RIS)

Abstract Utilizing energy-efficient, environmentally friendly, economic production processes and technologies to manufacture high magnetic induction grain-oriented silicon steel has become the focus of current research work. Based on using low-temperature slab reheating techniques to produce high magnetic induction grain-oriented silicon steel at both iron and steel enterprises and research institutions all over the world, the current application and exploitation was thoroughly generalized; the implementation methods for low-temperature slab reheating techniques by traditional process were also summarized. Furthermore, the recent developments of using thin slab casting and rolling process and twin-roll strip casting process to produce high magnetic induction grain-oriented silicon steel were presented. On these bases, the development trends of production process and technology for high magnetic induction grain-oriented silicon steel were analyzed.

Key words： high magnetic induction grain-oriented silicon steel low-temperature slab reheating technique compact production process inhibitor acquired inhibitor method

Received: 24 October 2012 Published: 21 March 2013

PACS:

TG142.7

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	FU Bing
	XIANG Li
	CHOU Ku-Tao
	CHENG Guo-Guang

Cite this article:

FU Bing,XIANG Li,CHOU Ku-Tao等. Recent Research Trends and Developments of Production Process and Technology for High Magnetic Induction Grain-Oriented Silicon Steel[J]. Iron and Steel, 2013, 48(3): 1-8.

URL:

http://www.chinamet.cn/Jweb_gt/EN/ OR http://www.chinamet.cn/Jweb_gt/EN/Y2013/V48/I3/1

[1]	陈卓，林勇．2011年度中国电工钢产业发展研究报告[R]．中国金属学会电工钢分会，2012，1．
[4]	李军，孙颖，赵宇，等．取向硅钢铸坯低温加热技术的开发进展[A]．第九届中国电工钢专业学术年会论文集[C]，2006：151．
[2]	仇圣桃，项利，岳尔斌，等．薄板坯连铸连轧流程生产取向硅钢技术分析[J]．钢铁，2008，43(9)：1．
[3]	李军，孙颖，赵宇，等．取向硅钢低温铸坯加热技术的研发进展[J]．钢铁，2007，42(10)：72．
[4]	李军，孙颖，赵宇，等．取向硅钢铸坯低温加热技术的开发进展[A]．第九届中国电工钢专业学术年会论文集[C]，2006：151．
[5]	T. Kumano, T. Haratani, N. Fujii. Effect of Nitriding on Grain Oriented Silicon Steel Bearing Aluminum[J]. ISIJ international, 2005, 45(1): 95.
[5]	T. Kumano, T. Haratani, N. Fujii. Effect of Nitriding on Grain Oriented Silicon Steel Bearing Aluminum[J]. ISIJ international, 2005, 45(1): 95.
[6]	T. Kumano, Y. Ohata, N. Fujii, et al. Effect of Nitriding on Grain Oriented Silicon Steel Bearing Aluminum(the second study)[J]. Journal of Magnetism and Magnetic Materials, 2006, (304): 602.
[6]	T. Kumano, Y. Ohata, N. Fujii, et al. Effect of Nitriding on Grain Oriented Silicon Steel Bearing Aluminum(the second study)[J]. Journal of Magnetism and Magnetic Materials, 2006, (304): 602.
[7]	N.Takahashi, J.Harase. Recent Development of Technology of Grain Oriented Silicon Steel[J]. Materials Science Forum, 1996, 204-206: 143.
[7]	N.Takahashi, J.Harase. Recent Development of Technology of Grain Oriented Silicon Steel[J]. Materials Science Forum, 1996, 204-206: 143.
[8]	N.Takahashi, Y.Suga, H.Kobayashi. Recent Developments in Grain-Oriented Silicon Steel[J]. Journal of Magnetism and Magnetic Materials, 1996, (160): 98.
[8]	N.Takahashi, Y.Suga, H.Kobayashi. Recent Developments in Grain-Oriented Silicon Steel[J]. Journal of Magnetism and Magnetic Materials, 1996, (160): 98.
[9]	T.Kubota, M.Fujikura, Y.Ushigami. Recent Progress and Future Trend on Grain-Oriented Silicon Steel[J]. Journal of Magnetism and Magnetic Materials, 2000, (215-216): 69.
[10]	熊野知二，村上健一，牛神义行．磁特性极优异的取向电磁钢板及其制造方法[P]．中国专利，CN101194032A．2008-06-04．
[11]	大畑喜史, 熊野知二, 藤井宣憲, ほか. 磁気特性に優れた一方向性電磁鋼板の製造方法[P]. 日本专利, 2001-152250, 2001-06-05.
[9]	T.Kubota, M.Fujikura, Y.Ushigami. Recent Progress and Future Trend on Grain-Oriented Silicon Steel[J]. Journal of Magnetism and Magnetic Materials, 2000, (215-216): 69.
[10]	熊野知二，村上健一，牛神义行．磁特性极优异的取向电磁钢板及其制造方法[P]．中国专利，CN101194032A．2008-06-04．
[11]	大畑喜史, 熊野知二, 藤井宣憲, ほか. 磁気特性に優れた一方向性電磁鋼板の製造方法[P]. 日本专利, 2001-152250, 2001-06-05.
[12]	Fritz B, Andreas B, Manfred E, et al. Process for the Production of Grain Oriented Magnetic Steel Sheets Having Improved Remagnetization Losses[P]. USP, 5711825, 1998-01-27.
[12]	Fritz B, Andreas B, Manfred E, et al. Process for the Production of Grain Oriented Magnetic Steel Sheets Having Improved Remagnetization Losses[P]. USP, 5711825, 1998-01-27.
[13]	Manfred E, Andreas B, Klaus G. Process for Producing a Grain-oriented Electrical Steel Sheet[P]. USP, 6153019, 2000-11-28.
[14]	峠哲雄, 村木峰男, 高島稔. 一方向性けい素鋼板の製造方法[P]. 日本专利, 平10-30124, 1998-02-03.
[13]	Manfred E, Andreas B, Klaus G. Process for Producing a Grain-oriented Electrical Steel Sheet[P]. USP, 6153019, 2000-11-28.
[15]	本田厚人, 峠哲雄, 定広健一, ほか. 高磁場特性に比較して低磁場特性に優れた方向性電磁鋼板の製造方法[P]. 日本专利, 平10-130728, 1998-05-19.
[14]	峠哲雄, 村木峰男, 高島稔. 一方向性けい素鋼板の製造方法[P]. 日本专利, 平10-30124, 1998-02-03.
[15]	本田厚人, 峠哲雄, 定広健一, ほか. 高磁場特性に比較して低磁場特性に優れた方向性電磁鋼板の製造方法[P]. 日本专利, 平10-130728, 1998-05-19.
[16]	峠哲雄, 定広健一, 本田厚人, ほか. 高磁場鉄損特性に比較して低磁場鉄損特性に優れた方向性電磁鋼板の製造方法[P]. 日本专利, 平10-259423, 1998-09-29.
[16]	峠哲雄, 定広健一, 本田厚人, ほか. 高磁場鉄損特性に比較して低磁場鉄損特性に優れた方向性電磁鋼板の製造方法[P]. 日本专利, 平10-259423, 1998-09-29.
[17]	本田厚人, 峠哲雄, 渡辺誠, ほか. 低磁場高周波での磁気特性及び打ち抜き加工性に優れる方向性けい素鋼板及びその製造方法[P]. 日本专利, 2000-256810, 2000-09-19.
[17]	本田厚人, 峠哲雄, 渡辺誠, ほか. 低磁場高周波での磁気特性及び打ち抜き加工性に優れる方向性けい素鋼板及びその製造方法[P]. 日本专利, 2000-256810, 2000-09-19.
[18]	胡卓超，李国保，孙涣德．一种高磁感取向硅钢及其生产方法[P]．中国专利，CN101353760A．2009-01-28．
[18]	胡卓超，李国保，孙涣德．一种高磁感取向硅钢及其生产方法[P]．中国专利，CN101353760A．2009-01-28．
[19]	Bayay J C，Poissonnet L，Castel J，等．特别是用于变压器的晶粒取向电工钢板的制造方法[P]．中国专利，CN1148411A．1997-04-23．
[19]	Bayay J C，Poissonnet L，Castel J，等．特别是用于变压器的晶粒取向电工钢板的制造方法[P]．中国专利，CN1148411A．1997-04-23．
[20]	Bayay J C，Castel J，Messeant F，等．特别是用于制造变压器磁路的晶粒取向电工钢板的制备方法[P]．中国专利，CN1220704A．1999-06-23．
[20]	Bayay J C，Castel J，Messeant F，等．特别是用于制造变压器磁路的晶粒取向电工钢板的制备方法[P]．中国专利，CN1220704A．1999-06-23．
[21]	屋鋪裕義, 金子輝雄. 方向性電磁鋼板およびその製造方法[P]. 日本专利, 平6-17201, 1994-01-25.
[21]	屋鋪裕義, 金子輝雄. 方向性電磁鋼板およびその製造方法[P]. 日本专利, 平6-17201, 1994-01-25.
[22]	屋鋪裕義, 田中隆. 方向性電磁鋼板およびその製造方法[P]. 日本专利, 平6-184707, 1994-07-05.
[22]	屋鋪裕義, 田中隆. 方向性電磁鋼板およびその製造方法[P]. 日本专利, 平6-184707, 1994-07-05.
[23]	屋鋪裕羲, 金子輝雄. 方向性電磁鋼板の製造方法[P]. 日本专利, 平3-111516, 1991-05-13.
[23]	屋鋪裕羲, 金子輝雄. 方向性電磁鋼板の製造方法[P]. 日本专利, 平3-111516, 1991-05-13.
[24]	屋鋪裕羲, 金子輝雄. 打抜き性の優れた方向性電磁鋼板の製造方法[P]. 日本专利, 平4-259329, 1992-09-14.
[24]	屋鋪裕羲, 金子輝雄. 打抜き性の優れた方向性電磁鋼板の製造方法[P]. 日本专利, 平4-259329, 1992-09-14.
[25]	屋鋪裕義, 金子輝雄. 方向性電磁鋼板およびその製造方法[P]. 日本专利, 平5-9666, 1993-01-19.
[25]	屋鋪裕義, 金子輝雄. 方向性電磁鋼板およびその製造方法[P]. 日本专利, 平5-9666, 1993-01-19.
[26]	何忠治．电工钢（第一版）[M]．北京：冶金工业出版社，1997．
[26]	何忠治．电工钢（第一版）[M]．北京：冶金工业出版社，1997．
[27]	牛神义行，中村修一，村上健一，等．高磁通密度取向电工钢板的制造方法[P]．中国专利，CN1351186A．2002-05-29．
[27]	牛神义行，中村修一，村上健一，等．高磁通密度取向电工钢板的制造方法[P]．中国专利，CN1351186A．2002-05-29．
[28]	高橋延幸, 菅洋三, 黒木克郎. 磁束密度の高い一方向性素鋼板の製造方法[P]. 日本专利, 平1-230721, 1989-09-14.
[28]	高橋延幸, 菅洋三, 黒木克郎. 磁束密度の高い一方向性素鋼板の製造方法[P]. 日本专利, 平1-230721, 1989-09-14.
[29]	高橋延幸, 黒木克郎, 新井聡. 磁束密度の高い一方向性電磁鋼板の製造方法[P]. 日本专利, 平1-283324, 1989-11-14.
[29]	高橋延幸, 黒木克郎, 新井聡. 磁束密度の高い一方向性電磁鋼板の製造方法[P]. 日本专利, 平1-283324, 1989-11-14.
[30]	高橋延幸, 菅洋三, 黒木克郎. 磁束密度の高い一方向性素鋼板の製造方法[P]. 日本专利, 平1-301820, 1989-12-06.
[30]	高橋延幸, 菅洋三, 黒木克郎. 磁束密度の高い一方向性素鋼板の製造方法[P]. 日本专利, 平1-301820, 1989-12-06.
[31]	吉冨康成, 黒木克郎, 松尾征夫, ほか. 磁気特性の優れた一方向性電磁鋼板の製造方法[P]. 日本专利, 平5-295438, 1993-11-09.
[31]	吉冨康成, 黒木克郎, 松尾征夫, ほか. 磁気特性の優れた一方向性電磁鋼板の製造方法[P]. 日本专利, 平5-295438, 1993-11-09.
[32]	李青山，韩赞熙，禹宗秀，等．基于低温板坯加热法生产具有高磁感应强度的晶粒择优取向电工钢板的方法[P]．中国专利，CN1231001A．1999-10-06．
[32]	李青山，韩赞熙，禹宗秀，等．基于低温板坯加热法生产具有高磁感应强度的晶粒择优取向电工钢板的方法[P]．中国专利，CN1231001A．1999-10-06．
[33]	Lee C S, Han C H, Woo J S. Method for Manufacturing High Magnetic Flux Density Grain Oriented Electrical Steel Based on Low Temperature Slab Heating Method[P]. USP, 6451128, 2002-09-17.
[33]	Lee C S, Han C H, Woo J S. Method for Manufacturing High Magnetic Flux Density Grain Oriented Electrical Steel Based on Low Temperature Slab Heating Method[P]. USP, 6451128, 2002-09-17.
[34]	路林林，李国保，孙涣德，等．一种具有良好底层的低温加热生产取向硅钢的方法[P]．中国专利，CN1978707A．2007-06-13．
[34]	路林林，李国保，孙涣德，等．一种具有良好底层的低温加热生产取向硅钢的方法[P]．中国专利，CN1978707A．2007-06-13．
[35]	张丕军，刘献东，陈晓，等．一种取向硅钢及其生产方法和装置[P]．中国专利，CN1796587A．2006-07-05．
[35]	张丕军，刘献东，陈晓，等．一种取向硅钢及其生产方法和装置[P]．中国专利，CN1796587A．2006-07-05．
[36]	王若平，毛炯辉，方泽民，等．低渗氮量高磁感取向硅钢带的生产方法[P]．中国专利，CN101775548A．2010-07-14．
[36]	王若平，毛炯辉，方泽民，等．低渗氮量高磁感取向硅钢带的生产方法[P]．中国专利，CN101775548A．2010-07-14．
[37]	王若平，毛炯辉，方泽民，等．高磁感取向硅钢带的生产方法[P]．中国专利，CN101775547A．2010-07-14．
[37]	王若平，毛炯辉，方泽民，等．高磁感取向硅钢带的生产方法[P]．中国专利，CN101775547A．2010-07-14．
[38]	倪献娟，夏兆所，周谊军，等．一种低温取向电工钢的生产方法[P]．中国专利，CN101358273A．2009-02-04．
[38]	倪献娟，夏兆所，周谊军，等．一种低温取向电工钢的生产方法[P]．中国专利，CN101358273A．2009-02-04．
[39]	夏兆所，倪献娟，许学勇，等．一种低温取向电工钢的生产方法[P]．中国专利，CN101348854A．2009-01-21．
[39]	夏兆所，倪献娟，许学勇，等．一种低温取向电工钢的生产方法[P]．中国专利，CN101348854A．2009-01-21．
[40]	蒋奇武，金文旭，庞树芳，等．一种低温加热生产高磁感取向硅钢的方法[P]．中国专利，CN101748259A．2010-06-23．
[40]	蒋奇武，金文旭，庞树芳，等．一种低温加热生产高磁感取向硅钢的方法[P]．中国专利，CN101748259A．2010-06-23．
[41]	Chun-Chih Liao, Chun-Kan Hou. Effect of Nitriding Time on Secondary Recrystallization Behaviors and Magnetic Properties of Grain-Oriented Electrical Steel[J]. Journal of Magnetism and Magnetic Materials, 2010, (322): 434.
[41]	Chun-Chih Liao, Chun-Kan Hou. Effect of Nitriding Time on Secondary Recrystallization Behaviors and Magnetic Properties of Grain-Oriented Electrical Steel[J]. Journal of Magnetism and Magnetic Materials, 2010, (322): 434.
[42]	Chine-Chih Chen, Chun-Kan Hou. Effect of Aluminum Content on the Secondary Recrystallization Behaviors of Grain Oriented Electrical Steels[J]. CAMP-ISIJ, 2010, 23: 186.
[42]	Chine-Chih Chen, Chun-Kan Hou. Effect of Aluminum Content on the Secondary Recrystallization Behaviors of Grain Oriented Electrical Steels[J]. CAMP-ISIJ, 2010, 23: 186.
[43]	吴忠旺，李军，赵宇，等．低温板坯加热技术取向硅钢脱碳及渗氮工艺与组织研究[A]．第十一届中国电工钢专业学术年会论文集[C]，2010：172．
[43]	吴忠旺，李军，赵宇，等．低温板坯加热技术取向硅钢脱碳及渗氮工艺与组织研究[A]．第十一届中国电工钢专业学术年会论文集[C]，2010：172．
[44]	吴忠旺，李军，赵宇，等．后天抑制剂获得法制取向硅钢析出物的转化规律[J]．钢铁研究学报，2011，23（12）：45．
[44]	吴忠旺，李军，赵宇，等．后天抑制剂获得法制取向硅钢析出物的转化规律[J]．钢铁研究学报，2011，23（12）：45．
[45]	吴忠旺，赵宇，李军，等．低温取向硅钢高温退火抑制剂的演化[J]．材料热处理学报，2011，32（11）：84．
[45]	吴忠旺，赵宇，李军，等．低温取向硅钢高温退火抑制剂的演化[J]．材料热处理学报，2011，32（11）：84．
[46]	吴忠旺，赵宇，李军，等．后天抑制剂取向硅钢析出物的研究[J]．材料工程，2012，（7）：55．
[46]	吴忠旺，赵宇，李军，等．后天抑制剂取向硅钢析出物的研究[J]．材料工程，2012，（7）：55．
[47]	何忠治，李军．近年来国外电工钢技术发展趋势[J]．电工钢，2004，（1）：2．
[47]	何忠治，李军．近年来国外电工钢技术发展趋势[J]．电工钢，2004，（1）：2．
[48]	铃木隆史等．无抑制剂的Hi-B硅钢生产方法[A]．第九届中国电工钢专业学术年会论文集[C]，2006：65．
[48]	铃木隆史等．无抑制剂的Hi-B硅钢生产方法[A]．第九届中国电工钢专业学术年会论文集[C]，2006：65．
[49]	早川康之, 黒沢光正, 小松原道郎. 方向性電磁鋼板の製造方法[P]. 日本专利, 2000-129356, 2000-05-09.
[49]	早川康之, 黒沢光正, 小松原道郎. 方向性電磁鋼板の製造方法[P]. 日本专利, 2000-129356, 2000-05-09.
[50]	早川康之, 岡部誠司, 山上日出雄, ほか. 下地被膜を有しない、磁束密度の高い方向性電磁鋼板の製造方法[P]. 日本专利, 2003-034821, 2003-02-07.
[50]	早川康之, 岡部誠司, 山上日出雄, ほか. 下地被膜を有しない、磁束密度の高い方向性電磁鋼板の製造方法[P]. 日本专利, 2003-034821, 2003-02-07.
[51]	早川康之, 山上日出雄, 高島稔, ほか. 下地被膜を有しない、磁束密度が高くかつ鉄損の低い方向性電磁鋼板の製造方法[P]. 日本专利, 2003-201516, 2003-07-18.
[51]	早川康之, 山上日出雄, 高島稔, ほか. 下地被膜を有しない、磁束密度が高くかつ鉄損の低い方向性電磁鋼板の製造方法[P]. 日本专利, 2003-201516, 2003-07-18.
[52]	Fortunati S，CIcale S，Abbruzzese G，等．晶粒取向硅钢的处理工艺[P]．中国专利，CN1244220A．2000-02-09．
[52]	Fortunati S，CIcale S，Abbruzzese G，等．晶粒取向硅钢的处理工艺[P]．中国专利，CN1244220A．2000-02-09．
[53]	Fortunati S，CIcale S，Abbruzzese G．晶粒取向电工钢片生产中控制抑制作用的工艺[P]．中国专利，CN1249007A．2000-03-29．
[53]	Fortunati S，CIcale S，Abbruzzese G．晶粒取向电工钢片生产中控制抑制作用的工艺[P]．中国专利，CN1249007A．2000-03-29．
[54]	CIcale S，Fortunati S，Abbruzzese G．晶粒取向电工钢板生产中控制抑制作用的方法[P]．中国专利，CN1249008A．2000-03-29．
[54]	CIcale S，Fortunati S，Abbruzzese G．晶粒取向电工钢板生产中控制抑制作用的方法[P]．中国专利，CN1249008A．2000-03-29．
[55]	Fortunati S，CIcale S，Abbruzzese G．由薄板坯生产晶粒取向电工钢带的方法[P]．中国专利，CN1231703A．1999-10-13．
[55]	Fortunati S，CIcale S，Abbruzzese G．由薄板坯生产晶粒取向电工钢带的方法[P]．中国专利，CN1231703A．1999-10-13．
[56]	Fortunati S，CIcale S，Abbruzzese G．用薄板坯生产具有高的磁性能的晶粒取向电工钢带的工艺[P]．中国专利，CN1228817A．1999-09-15．
[56]	Fortunati S，CIcale S，Abbruzzese G．用薄板坯生产具有高的磁性能的晶粒取向电工钢带的工艺[P]．中国专利，CN1228817A．1999-09-15．
[57]	Gunther Klaus, Lahn ludger, Ploch Andreas. Method for Producing a Grain-Oriented Electrical Steel Strip [P]. CA 2615586, 2007-02-08.
[57]	Gunther Klaus, Lahn ludger, Ploch Andreas. Method for Producing a Grain-Oriented Electrical Steel Strip [P]. CA 2615586, 2007-02-08.
[58]	Gunther Klaus, Lahn Ludger, Ploch Andreas. 生产晶粒取向的电工带钢的方法[P]．中国专利，CN101238227A．2008-08-06．
[58]	Gunther Klaus, Lahn Ludger, Ploch Andreas. 生产晶粒取向的电工带钢的方法[P]．中国专利，CN101238227A．2008-08-06．
[59]	项利．薄板坯连铸连轧流程生产取向硅钢（27Q140）的实验研究[D]．博士学位论文．北京：钢铁研究总院．2008．
[59]	项利．薄板坯连铸连轧流程生产取向硅钢（27Q140）的实验研究[D]．博士学位论文．北京：钢铁研究总院．2008．
[60]	肖丽俊．薄板坯连铸连轧流程制造高磁感取向硅钢（30QG130）的实验研究[D]．博士学位论文．北京：钢铁研究总院．2009．
[60]	肖丽俊．薄板坯连铸连轧流程制造高磁感取向硅钢（30QG130）的实验研究[D]．博士学位论文．北京：钢铁研究总院．2009．
[61]	董廷亮．“TSCR+渗氮”工艺试制Hi-B钢中AlN的析出行为研究[D]．博士学位论文．北京：钢铁研究总院．2011．
[61]	董廷亮．“TSCR+渗氮”工艺试制Hi-B钢中AlN的析出行为研究[D]．博士学位论文．北京：钢铁研究总院．2011．
[62]	肖丽俊，岳尔斌，仇圣桃，等．双辊薄带连铸生产取向硅钢的技术分析[J]．钢铁研究学报，2009，21(8)：1．
[62]	肖丽俊，岳尔斌，仇圣桃，等．双辊薄带连铸生产取向硅钢的技术分析[J]．钢铁研究学报，2009，21(8)：1．
[63]	I. Iwanaga, K. Iwayama, K. Miyazawa, et al. Process for Producing a Grain-Oriented Electrical Sheet by Means of Rapid Quenched-Solidification Process[P]. USP, 5049204, 1991-09-17.
[63]	I. Iwanaga, K. Iwayama, K. Miyazawa, et al. Process for Producing a Grain-Oriented Electrical Sheet by Means of Rapid Quenched-Solidification Process[P]. USP, 5049204, 1991-09-17.
[64]	I. Iwanaga, K. Iwayama. Method of Producing Grain Oriented Electrical Steel Sheet Having High Magnetic Flux[P]. USP, 5051138, 1991-09-24.
[64]	I. Iwanaga, K. Iwayama. Method of Producing Grain Oriented Electrical Steel Sheet Having High Magnetic Flux[P]. USP, 5051138, 1991-09-24.
[65]	Stefano Fortunati, Stefano Cicale, Giuseppe Abbruzzese. Process for the Production of Grain-Oriented Electrical Steel Strips[P]. USP, 6964711, 2005-11-15.
[65]	Stefano Fortunati, Stefano Cicale, Giuseppe Abbruzzese. Process for the Production of Grain-Oriented Electrical Steel Strips[P]. USP, 6964711, 2005-11-15.
[66]	Jerry W.Schoen, Robert S.Williams, Glenn S.Huppi. Method of Continuously Casting Electrical Steel Strip With Controlled Spray Cooling[P]. USP, 6739384, 2004-05-25.
[66]	Jerry W.Schoen, Robert S.Williams, Glenn S.Huppi. Method of Continuously Casting Electrical Steel Strip With Controlled Spray Cooling[P]. USP, 6739384, 2004-05-25.
[67]	Klaus Günther, Giuseppe Abbruzzese, Stefano Fortunati, et al. Recent Technology Developments in the Production of Grain-Oriented Electrical Steel[J]. Steel Reasearch International. 2005, (5): 413.
[67]	Klaus Günther, Giuseppe Abbruzzese, Stefano Fortunati, et al. Recent Technology Developments in the Production of Grain-Oriented Electrical Steel[J]. Steel Reasearch International. 2005, (5): 413.