Movement of Scrap in the Bath of Converter |
YANG Wen-yuan1,ZHANG Xian-gui2,WANG Ming-lin1,GAO Wei-tao1,CUI Huai-zhou1, BAI Yu1 |
1. Central Iron and Steel Research Institute, China Iron and Steel Research Institute Group, Beijing 100081, China 2. Steelmaking Plant, Wuhan Iron and Steel Group Co., Wuhan 430080, Hubei, China |
|
|
Abstract The injection parameter of water mold was calculated based on similarity principle. The actual situation of the movement of scrap in molten bath of the converter was simulated for the first time.The impact of scrap on mixing time and splashing was measured. If there are 10% scrap in large converter, the molten bath mixing time is longer 35.3% than no scrap in converter. In hot metal dephosphorization pretreatment converter, 10% scrap will prolong bath mixing time 62.8%. The relationship between the weight of scrap and suspended energy in bath was quantitatively studied. In order to be in good dynamics condition for scrap melting, the stirring energy of the bath should not be less than a large piece of scrap suspension energy. These could supplement the basic knowledge of scrap melting and provide the guidance for the use of scrap in the converter and the optimization of the converter blowing process.
|
Received: 18 June 2012
Published: 21 March 2013
|
|
|
|
|
[1] |
SHANGGUAN Fang-qin, LI Xiu-ping, ZHOU Ji-cheng, WANG Fang-jie, BU Qing-cai, ZHANG Chun-xia. Strategic research on development of steel scrap resources in China[J]. Iron and Steel, 2020, 55(6): 8-14. |
[2] |
LI Lin, LI Ming-ming, LI Qiang, ZOU Zong-shu. Melt splashing behavior of steelmaking converter with nozzle-twisted lance[J]. Iron and Steel, 2020, 55(6): 54-60. |
[3] |
YANG Li-bin, ZENG Jia-qing, DENG Yong, XU Xiao-wei, WU Li-ping. Highly efficiency and long-life combined blowing technology of big converter[J]. Iron and Steel, 2020, 55(4): 45-52. |
[4] |
DONG Wen-liang, PAN Hong-wei, LUO Lei, JI Chen-xi, LI Hai-bo, TIAN Zhi-hong. Phosphorous distribution in dephosphorization slag[J]. Iron and Steel, 2020, 55(2): 75-81. |
[5] |
ZHOU Zhenyu, TANG Ping, ZHOU Zunchuan, HOU Zibing, WEN Guanghua. Optimization on nozzle parameters of 200 t combined blowing vanadium extraction converter[J]. Iron and Steel, 2019, 54(9): 50-56. |
[6] |
WANG Xinjiang. Technological progress of EAF steelmaking in China[J]. Iron and Steel, 2019, 54(8): 1-8. |
|
|
|
|