Effect of Cooling Process After Rolling on Microstructure and Mechanical Property of Nb-Ti Microalloyed |
Low-Carbon Bainite SteelLI De-fa1,2,WANG Shi-sen2,XIONG Yu-zhang2,XING Shu-qing1,XIONG Tao2,YU Hong-wei2 |
1. Materials and Metallurgy School, UST Inner Mongolia, Baotou 014010, Nei Mongol, China 2. Research Institute, Wuhan Iron and Steel Group Corp., Wuhan 430080, Hubei, China |
|
|
Abstract The effects of cooling process after rolling on microstructure, precipitated phase and mechanical properties of low-carbon bainite steel were investigated by method of SEM and TEM. The results show that ferrite and bainite dual phases can be obtained with air-cooling and accelerated cooling process after hot-rolled. The percentage of ferrite phase increases with the end of air-cooling temperature reduced, the size of ferrite and precipitated phase is larger, the lath of bainite is sharper and the edge is clearer. The shape of M/A constituent is film-like and changes with temperature. When temperature of completion in air-cooling are between 725℃ and 740℃, then it is cooled to 440℃ with cooling rate of 15℃/s, the comprehensive mechanical properties are excellent and can reach the requirements of Q690 of GB/T1591.
|
Received: 19 June 2012
Published: 21 March 2013
|
|
|
|
|
[1] |
DU Liang, HAN Xiu-li, ZHANG Quan-sheng, ZHOU Xiang, YANG Hong-da, WANG Ying. Quantitative relation between mineralogical structure and metallurgical properties of sinter of import iron ore[J]. Iron and Steel, 2020, 55(6): 38-45. |
[2] |
SUN Chao-fan, FANG Yuan, WANG Ya-qing, LIU Wei. Influence of temper rolling reduction rate on microstructure and mechanical properties of TS290 steel[J]. Iron and Steel, 2020, 55(6): 75-79. |
[3] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
[4] |
JIANG Yue-yue, WANG Zhao-dong, DENG Xiang-tao. Effect of trace rare earth Ce on martensitic transformation behavior of ultra-high strength low alloy steel[J]. Iron and Steel, 2020, 55(6): 84-90. |
[5] |
WU Zhi-guang, GONG Xue-ting, LI Xin, ZHAO Ji-qing, GONG Zhi-hua. Effect of heat treatment process on creep-rupture property of 20Cr1Mo1VTiB bolt steel[J]. Iron and Steel, 2020, 55(6): 101-106. |
[6] |
SHAO Chun-juan,ZHEN Fan,ZHANG Ji-ming,QU Jin-bo,ZHANG Lei. Effect of sample thinning on DWTT property of heavy wall X80 steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 497-504. |
|
|
|
|