Optimization of Slag System in Decarburization Converter of Duplex Process With Low Silicon Semi-Steel Smelting |
LIN Teng-chang1,ZHU Rong1,LU Zhi-fang1,FANG Yu-rong2,WANG Cheng-jie1 |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China 2. Steelmaking Plant, Minguang Co., Ltd., Fujian Sansteel, Sanming 365000, Fujian, China |
|
|
Abstract In order to decrease stick lance and reduce the end phosphorus content, the slag system of 120t duplex process decarburization converter was studied by using chemical analysis, melting experiment and Factsage thermodynamic numerical simulation. The effect of slag system on smooth smelting was expounded, and a basic principle and final slag composition of new slag system was established. After the industrial application of new slag system, the phenomenon of stick lance remits to a certain extent. The slag ratio can reduce to 34.7kg/t of decarburization converter, and the end phosphorus content is about 0.006%-0.012%.
|
Received: 20 September 2012
Published: 28 May 2013
|
|
|
|
[1] |
潘秀兰,王艳红,梁慧智等. 转炉双联法炼钢工艺的新进展[J].鞍钢技术,2007,5:5-10.
|
[2] |
杨素波,张大德,文永才等. 攀钢半钢炼钢技术进步及效果[J].钢铁,2003,38(1):13-15.
|
[2] |
杨素波,张大德,文永才等. 攀钢半钢炼钢技术进步及效果[J].钢铁,2003,38(1):13-15.
|
[3] |
文永才,董履仁,杨素波等. 攀钢半钢炼钢转炉溅渣护炉技术研究[J].钢铁,2003,38(2):16-18.
|
[4] |
杜建良. 大锥度锥体氧枪研发及在半钢炼钢条件下的应用[J].钢铁,2009,44(7):39-42.
|
[5] |
李伟东,辛国强,工成青. 鞍钢180t转炉锥体氧枪的研制与应用[J].鞍钢技术,2011,4:15-17.
|
[3] |
文永才,董履仁,杨素波等. 攀钢半钢炼钢转炉溅渣护炉技术研究[J].钢铁,2003,38(2):16-18.
|
[6] |
丁满堂. 半钢炼钢复吹工艺优化[J].钢铁,2009,44(5):32-34.
|
[4] |
杜建良. 大锥度锥体氧枪研发及在半钢炼钢条件下的应用[J].钢铁,2009,44(7):39-42.
|
[5] |
李伟东,辛国强,工成青. 鞍钢180t转炉锥体氧枪的研制与应用[J].鞍钢技术,2011,4:15-17.
|
[7] |
许立志. 半钢炼钢转炉增大供氧强度的氧枪设计与使用[J].钢铁钒钛,2005,26(3):60-63.
|
[8] |
谢淑芳,郑忠,张涛. 转炉半钢炼钢造渣料计算模型[J].钢铁,2010,45(12):37-40.
|
[9] |
孟劲松,姜茂发,朱英雄. 复吹转炉应用无氟造渣剂一一铁矾土的生产实践[J].炼钢,2005,21(2):1-3.
|
[6] |
丁满堂. 半钢炼钢复吹工艺优化[J].钢铁,2009,44(5):32-34.
|
[7] |
许立志. 半钢炼钢转炉增大供氧强度的氧枪设计与使用[J].钢铁钒钛,2005,26(3):60-63.
|
[10] |
岑永权,陈麒忠. 转炉初渣熔点正交试验[J].江西冶金,1991,11(1):50-54.
|
[8] |
谢淑芳,郑忠,张涛. 转炉半钢炼钢造渣料计算模型[J].钢铁,2010,45(12):37-40.
|
[9] |
孟劲松,姜茂发,朱英雄. 复吹转炉应用无氟造渣剂一一铁矾土的生产实践[J].炼钢,2005,21(2):1-3.
|
[10] |
岑永权,陈麒忠. 转炉初渣熔点正交试验[J].江西冶金,1991,11(1):50-54.
|
[11] |
兰杰,丁文江,姜周华等. CaO-A12O3-CaF2-SiO2-MgO精炼渣系起泡性能与炉渣物理性质的关系[J].特殊钢,1999,20 (1):15-17.
|
[11] |
兰杰,丁文江,姜周华等. CaO-A12O3-CaF2-SiO2-MgO精炼渣系起泡性能与炉渣物理性质的关系[J].特殊钢,1999,20 (1):15-17.
|
[12] |
栾秋生,文永才,汤天宇等. 攀钢炼钢复合造渣剂的研制及应用[J].钢铁钒钛,2000, 21(4):55-58.
|
[12] |
栾秋生,文永才,汤天宇等. 攀钢炼钢复合造渣剂的研制及应用[J].钢铁钒钛,2000, 21(4):55-58.
|
[13] |
曹东,李德刚,廖相巍等. 造渣制度影响转炉深脱磷实验研究[J].炼钢,2009,25(6):43-45.
|
[13] |
曹东,李德刚,廖相巍等. 造渣制度影响转炉深脱磷实验研究[J].炼钢,2009,25(6):43-45.
|
[1] |
HUANG Bing,ZHU Ming-mei,ZHONG Yong,ZHANG Ai-ping,WANG Yu. Thermodynamic calculation of phase composition of CaOSiO2FeOCr2O3MgOMnO slag system[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 718-725. |
[2] |
KANG Wei1, JIN You-lin2. Inclusions control in anti-fatigue stress steel[J]. Iron and Steel, 2019, 54(5): 27-31. |
[3] |
LI Qiu-han1,2, JIA Ya-nan1,2, ZHANG Chao-jie1,2, CHEN Bin1,2, GUO Zi-feng1,2, GUO Jia1,2. Viscosity-structure analysis of CaO-SiO2-MgO-Al2O3-Cr2O3 slags and application of Iida model[J]. Iron and Steel, 2019, 54(4): 99-105. |
[4] |
WANG Zhe,TANG Ping,MI Xiao-xi,HU Quan,LU Yi-fan,WEN Guang-hua. Effect of[w((CaF2))]on crystallization properties of CaO-SiO2-Al2O3 based mold fluxes[J]. Iron and Steel, 2018, 53(7): 38-44. |
[5] |
DENG Jian-jun,ZHANG Ming-bo,LI Jian-xin,QIU Sheng-tao,WANG Shi-zhao,NING Shu-bo. Thermodynamics of dephosphorization capacity of containing TiO2 and Al2O3 of CaO-based semi-steel slag[J]. Iron and Steel, 2018, 53(3): 27-37. |
[6] |
LIANG Xin-teng,,SUN Yan-hui,ZENG Jian-hua,CHEN Jun,CHEN Lu. Theoretical?research?and application of less slag steelmaking of semi-steel in BOF of Pansteel[J]. Iron and Steel, 2017, 52(7): 47-51. |
|
|
|
|