Application of Controlled Cooling Process After Normalizing in the Development of Heavy Gauge Ship Plate |
LI Xin-lei,YANG Chun-wei |
Qinhuangdao Shouqin Metal Materials Co., Ltd., Qinhuangdao 066326, Hebei, China |
|
|
Abstract The controlled cooling process after normalizing is the combined process of cooling process and normalizing. Because the temperature of austenization is as the same as the normalizing, the finer microstructure of ferrite and pearlite can be obtained after water cooling. Experimental study was performed in the development of 120mm E36 ship plate steel, and the “weak water-cooling” model of quenching experiment was used after normalizing. The final cooling temperature was between 600℃ and 650℃. Compared with the traditional air cooling after normalizing, the plasticity doesn’t decrease, and the strength increases by about 15MPa. Low-temperature toughness is good, especially the -60℃ impact energy in the center is over 100J. The more fine and uniform ferrite-pearlite microstructure can be obtained by experiment. The mechanical properties index can meet the standard requirement of E36 ship plate. The results have important significance in the development of heavy gauge ship plate.
|
Received: 16 July 2012
Published: 28 May 2013
|
|
|
|
[1] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
[2] |
ZHAO Yun-peng, YU Chao, XIAO Hong, WU Zong-he, XU Peng-peng, XIE Hong-biao. Effect of pure iron interlayer on mechanical properties of hot rolled stainless steel clad plate[J]. Iron and Steel, 2020, 55(5): 73-79. |
[3] |
SHAO Cheng-wei, WANG Jun-tao, ZHAO Xiao-li, HUI Wei-jun. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93. |
[4] |
CAO Jing-hua1,PAN Hong-bo2,3,ZHANG Jing1,ZHANG Teng-fei2,LI Xu-dong2,LIU Wei-ming2,3. Continuous cooling transformation of NbTi microcarbon deep drawing dualphase steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 322-328. |
[5] |
WANG Ji-hong, ZHANG Li-na, CHEN De-li, QI Yue, CAO Li-hong. Discussion about heat treatment process of X20Cr13 blade steel for gas turbine[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 18-. |
[6] |
XING Xian-qiang, CAO Wen-quan, WANG Cun-yu. Bond structure of 55SiCr steel used for coil springs of automotive suspension system[J]. Iron and Steel, 2020, 55(3): 68-73. |
|
|
|
|