铸态超级双相不锈钢S32750热加工性能

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (0 KB) HTML (0 KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to investigate the hot deformation behavior and microstructure evolution of as-cast S32750 super duplex stainless steel, high temperature tensile tests and compression tests were carried out at different temperatures(900-1200℃) and strain rates(0.1-25s-1) by Gleeble-3800 thermo-mechanical simulator. High temperature tensile tests show that S32750 has good ductility from 1000℃ to 1200℃. The flow behavior of S32750 was investigated by high temperature compression tests. The flow curves of low temperatures and slow strain rates exhibit a particularly yield-point-elongation-like effect, which is different from single phase stainless steel. The flow curves of high strain rates or high temperatures and slow strain rates were characterized by recrystallization. The microstructure evolution shows that dynamic recrystallization (DRX) can occur in both ferrite and austenite phases, and DRX in ferrite is prior to austenite. By increasing temperature and decreasing strain rate, DRX can be enhanced. Based on this，the hot deformation equation is set up, the apparent stress exponent is 3.99, and the apparent activation energy(Q) is 393.75kJ/mo1. Its softening mechanism varies with Zener-Hollomon parameter (abbreviated Z) in the above mentioned deformation conditions, and with increasing Z parameter, the peak stress of hot deformation increases．

Key words： S32750 hot ductility true strain - true stress curves dynamic recrystallization hot deformation equation

Received: 17 August 2012 Published: 18 June 2013

PACS:

TG115.5

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WU Min
	LIAN Xiao-Ji
	ZENG Li
	LI Guo-Beng

Cite this article:

WU Min,LIAN Xiao-Ji,ZENG Li等. Investigation on Hot Workability of As-Cast S32750 Super Duplex Stainless Steel[J]. Iron and Steel, 2013, 48(6): 54-60.

URL:

http://www.chinamet.cn/Jweb_gt/EN/ OR http://www.chinamet.cn/Jweb_gt/EN/Y2013/V48/I6/54

[1]	陆世英.超级不锈钢和高镍耐蚀合金,北京：化学工业出版社[J].,2012,:-
[1]	陆世英.超级不锈钢和高镍耐蚀合金,北京：化学工业出版社[J].,2012,:-
[2]	I.Gurrappa,C.V. Krishna Reddy.Characterization of newly developed structural DMR-1700 steel and comparison with different steels for chemical applications[J].Journal of Materials Processing Technology,2007,182(1):195-
[2]	I.Gurrappa,C.V. Krishna Reddy.Characterization of newly developed structural DMR-1700 steel and comparison with different steels for chemical applications[J].Journal of Materials Processing Technology,2007,182(1):195-
[3]	Lin G,Zhang ZX,Song HW,Tong JR,Zhou CD.Investigation of the hot plasticity of duplex stainless steel[J].Journal of Iron and Steel Research,International,2008,15(6):83-
[3]	Lin G,Zhang ZX,Song HW,Tong JR,Zhou CD.Investigation of the hot plasticity of duplex stainless steel[J].Journal of Iron and Steel Research,International,2008,15(6):83-
[4]	Garzon,A.P. Tschiptschin.EBSD texture analysis of a high temperature gas nitrided duplex stainless steel[J].Materials Science and Engineering A,2006,441(1-2):230-
[4]	Garzon,A.P. Tschiptschin.EBSD texture analysis of a high temperature gas nitrided duplex stainless steel[J].Materials Science and Engineering A,2006,441(1-2):230-
[5]	J.Charles. 91 Stainless Steels. Proc. Conf.[J]., 1991,:-
[5]	J.Charles. 91 Stainless Steels. Proc. Conf.[J]., 1991,:-
[6]	Isabel Gutierrez et al.Duplex stainless steels. ISTE Ltd and John weily & Sone,Inc UK and USA[J].,2009,:-
[6]	Isabel Gutierrez et al.Duplex stainless steels. ISTE Ltd and John weily & Sone,Inc UK and USA[J].,2009,:-
[7]	Tan Hua,Jiang Yiming,Deng Bo.Effect of annealing temperature on the pitting corrosion resistance of super duplex stainless steel UNS S32750[J].Materials Characterization,2009,60(9):1049-
[7]	Tan Hua,Jiang Yiming,Deng Bo.Effect of annealing temperature on the pitting corrosion resistance of super duplex stainless steel UNS S32750[J].Materials Characterization,2009,60(9):1049-
[8]	Zou Dening,Han Ying,Zhang Wei.Sigma Phase Precipitation and Properties of Super-duplex Stainless Steel UNS S32750 Aged at the Nose Temperature[J].Journal of Wuhan University of Technology-materials Science Edition,2011,26(2):183-
[8]	Zou Dening,Han Ying,Zhang Wei.Sigma Phase Precipitation and Properties of Super-duplex Stainless Steel UNS S32750 Aged at the Nose Temperature[J].Journal of Wuhan University of Technology-materials Science Edition,2011,26(2):183-
[9]	Bonollo F.,Ferro P.,Cervo R. .Wire Metallurgical and mechanical characterization of UNS S32750 welded joints with innovative filler wire[J].Metallurgia Italiana,2009,10:55-
[9]	Bonollo F.,Ferro P.,Cervo R. .Wire Metallurgical and mechanical characterization of UNS S32750 welded joints with innovative filler wire[J].Metallurgia Italiana,2009,10:55-
[10]	王佳夫等.S32750 超级双相不锈钢的热变形及组织分析[J].东北大学学报（自然科学版）,2011,32(7):948-
[10]	王佳夫等.S32750 超级双相不锈钢的热变形及组织分析[J].东北大学学报（自然科学版）,2011,32(7):948-
[11]	谢世敬等.00Cr25Ni7Mo4N超级双相不锈钢的热变形行为[J].上海金属,2008,30(6):4-
[11]	谢世敬等.00Cr25Ni7Mo4N超级双相不锈钢的热变形行为[J].上海金属,2008,30(6):4-
[12]	不锈钢实用手册,北京,中国科学技术出版社[J].,2003,:785-
[12]	不锈钢实用手册,北京,中国科学技术出版社[J].,2003,:785-
[13]	A. Momeni,K. Dehghani,X. X. Zhang. Mechanical and microstructural analysis of 2205 duplex stainless steel under hot working condition[J].Journal of Materials Science,2012,47:2966-
[13]	A. Momeni,K. Dehghani,X. X. Zhang. Mechanical and microstructural analysis of 2205 duplex stainless steel under hot working condition[J].Journal of Materials Science,2012,47:2966-
[14]	A.Iza-Mendia,A. Pinol-Juez,J. J. Urcola,I. Gutiérrez.. Microstructural and mechanical behavior of a duplex stainless steel under hot working conditions[J].Metallurgical and Materials Transactions A,1998,29(12):2975-
[14]	A.Iza-Mendia,A. Pinol-Juez,J. J. Urcola,I. Gutiérrez.. Microstructural and mechanical behavior of a duplex stainless steel under hot working conditions[J].Metallurgical and Materials Transactions A,1998,29(12):2975-