Effect of Aluminum Content on Welding Property of 304, 316L Alloy Hot-Rolled Sheet |
LA Pei-qing,YAO Liang,MENG Qian,ZHOU Mao-xiong,WEI Yu-peng |
Key Laboratory of Nonferrous Metal Materials of Lanzhou University of Technology, Lanzhou 730050, Gansu, China |
|
|
Abstract The weldability of Al mass fraction 4% 304, 2% 316L stainless steel hot-rolled sheet was investigated. By using manually TIG, microstructure of weld joint was analyzed by optical microscopy, the distribution elements of welding base metal was measured by electron microprobe (EMPA) , mechanical properties of welded joints was also tested. The investigations of microstructure and mechanical properties show that the aluminum-containing 304 and 316L alloy hot-rolled plates are selected ER308L, ER316L as welding materials, after TIG welded, the weld area has no cracks, gas porosities and other defects, the joint has good strength and ductility, the mechanical properties of the weld joint is similar with the base metal. Heat-affected zone and base metal organization is basically the same, the fusion is well between the weld area and base metal, the microstructure is good, adding aluminum 304 and 316L stainless steel with good weldability.
|
Received: 04 February 2013
Published: 25 November 2013
|
|
|
|
|
[1] |
ZHAO Yun-peng, YU Chao, XIAO Hong, WU Zong-he, XU Peng-peng, XIE Hong-biao. Effect of pure iron interlayer on mechanical properties of hot rolled stainless steel clad plate[J]. Iron and Steel, 2020, 55(5): 73-79. |
[2] |
CAI Zhen, LIANG Wen, WANG Shui-ze, LIU Yong-qian. Discussion about practice and process of ferrite rolling in Ti-IF steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 7-. |
[3] |
ZHOU Cong-rui, CHEN Xiao-long, ZHOU Ming-ke,FAN Lei, MEI Peng, BAO Si-qian. Cause analysis of surface blackening of SPHC hot rolled strip after pickling[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 41-. |
[4] |
SUN Ming-han, ZHENG Yi, QU Chun-tao, JIN Shi-zhe, XU Zhi-qiang, DU Feng-shan. Numerical simulation of temperature field in ultra-fast cooling process of hot rolled plate[J]. Iron and Steel, 2020, 55(3): 50-57. |
[5] |
YANG Geng-wei1,HU Zhuo-li1,YIN Qi-long1,MAO Xin-ping1,2,MIAO Li-sha1,LIU Yang2. Effect of phase transformation time on microstructure and mechanical properties of hotrolled TRIP steel produced by CSP process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 143-149. |
[6] |
YI Ya-li, HAN Xiao-kai, ZHANG Lei, JIN He-rong. Homogeneity of grain structure for 316L/EH40 stainless steel clad plate during hot rolling process[J]. Iron and Steel, 2020, 55(1): 47-55. |
|
|
|
|