Thermodynamic Analysis on Direct Alloying of Molybdenum Oxide for Stainless Steel in AOD Furnace |
MA Deng,GUO Pei-min,PANG Jian-ming,ZHAO Pei |
(Center of Efficient Utilization of Resources by Low-Temperature Metallurgy,China Central Iron and Research Institute Group, Beijing 100081, China) |
|
|
Abstract The oxidation reaction of molybdenum and reduction reaction of molybdenum trioxide were discussed, and the effect of the addition of molybdenum oxide on AOD process and the component of liquid steel was also investigated. The subsequent research was focused on the volatilization of molybdenum oxide which had a serious impact on the recovery of molybdenum. Finally, thermodynamic analysis of “decarburization and molybdenum conservation” and “decarburization and chromium conservation”was accomplished. The direct alloying of molybdenum oxide in AOD is completely feasible, additional reducing agent and fixative agent, however, should be added to AOD, together with molybdenum oxide for higher recovery of molybdenum and better stainless steel.
|
Received: 06 June 2013
Published: 07 May 2014
|
|
|
|
[1] |
李正邦,郭培民,张和生,林功文.白钨矿和氧化钼直接还原和进化的理论分析及工业试验[J].钢铁,1999,34(10),20-23
|
[2] |
郭培民.白钨矿和氧化钼直接还原合金化冶炼合金钢的研究[D].北京:钢铁研究总院,2001
|
[1] |
李正邦,郭培民,张和生,林功文.白钨矿和氧化钼直接还原和进化的理论分析及工业试验[J].钢铁,1999,34(10),20-23
|
[3] |
郭培民,李正邦,林功文.发展钨精矿、氧化钼、钒渣直接合金化技术[J].钢铁研究学报,2000,21(4):23-25
|
[2] |
郭培民.白钨矿和氧化钼直接还原合金化冶炼合金钢的研究[D].北京:钢铁研究总院,2001
|
[3] |
郭培民,李正邦,林功文.发展钨精矿、氧化钼、钒渣直接合金化技术[J].钢铁研究学报,2000,21(4):23-25
|
[4] |
赵沛,成国光,沈苏.炉外精炼及铁水预处理实用技术手册[M].北京:冶金工业出版社,2007
|
[4] |
赵沛,成国光,沈苏.炉外精炼及铁水预处理实用技术手册[M].北京:冶金工业出版社,2007
|
[5] |
陈家祥.钢铁冶金学[M]. 北京:冶金工业出版社,2004
|
[5] |
陈家祥.钢铁冶金学[M]. 北京:冶金工业出版社,2004
|
[6] |
王新华.钢铁冶金-炼钢学[M]. 北京:高等教育出版社,2007
|
[6] |
王新华.钢铁冶金-炼钢学[M]. 北京:高等教育出版社,2007
|
[7] |
黄希祜,钢铁冶金原理[M].北京:冶金工业出版社,2002
|
[7] |
黄希祜,钢铁冶金原理[M].北京:冶金工业出版社,2002
|
[8] |
刘岩,姜茂发,许力贤,等.铬矿熔融还原不锈钢直接合金化的热力学分析[J].钢铁研究学报,2006,18(11):15-18
|
[8] |
刘岩,姜茂发,许力贤,等.铬矿熔融还原不锈钢直接合金化的热力学分析[J].钢铁研究学报,2006,18(11):15-18
|
[9] |
梁英教.无机物热力学数据手册[M].沈阳:东北大学出版社,1989
|
[9] |
梁英教.无机物热力学数据手册[M].沈阳:东北大学出版社,1989
|
[10] |
潘学峰,周海斌,朱苗勇.连铸中间包内钢液温度变化规律的研究[J].中国冶金,2007,17(10):45-49
|
[10] |
潘学峰,周海斌,朱苗勇.连铸中间包内钢液温度变化规律的研究[J].中国冶金,2007,17(10):45-49
|
[11] |
郭培民,赵沛,李正邦.添加剂对氧化钼(MoO3)高温会发的影响[J].特殊钢,2006,27(11):30-31
|
[11] |
郭培民,赵沛,李正邦.添加剂对氧化钼(MoO3)高温会发的影响[J].特殊钢,2006,27(11):30-31
|
[12] |
朱航宇,李正邦,杨海森,刘吉刚.CaCO3抑制三氧化钼挥发热力学及动力学分析[J].特殊钢,2012,33(1):12-14
|
[12] |
朱航宇,李正邦,杨海森,刘吉刚.CaCO3抑制三氧化钼挥发热力学及动力学分析[J].特殊钢,2012,33(1):12-14
|
[13] |
朱航宇,李正邦,杨海森,刘吉刚.三氧化钼低温挥发性能及抑制方法[J]. 钢铁研究学报,2012,24(7);10-12
|
[13] |
朱航宇,李正邦,杨海森,刘吉刚.三氧化钼低温挥发性能及抑制方法[J]. 钢铁研究学报,2012,24(7);10-12
|
|
|
|