Missile Detection Quickly Recover Practices of No.3 Blast Furnace With Copper Cooling Stave in TISCO |
XU Ji-shan |
(Taiyuan Iron and Steel Group Co., Ltd., Taiyuan 030003, Shanxi, China) |
|
|
Abstract Four layers of copper cooling stave were stalled from bosh to stack of No.3 blast furnace TISCO.Due to the high thermal conductivity of copper cooling stave,during blowing recovery after overhaul,some occurrences and accidents had to face,such as slag skin peeling,frequent fluctuations of heat load,even collapse and loss of gas of furnace cooling.According to the problems above mentioned,through stipulating for plan of the missile detection recovery in detailed,blowing air and enriched oxygen according to the target value,and quantificationally controlling the PCI,blast temperature,fuel ratio,hot metal and slag tapping,fast recovery of furnace conditions in 20-24 h can be achieved after above 35 h missile detection.
|
Received: 04 July 2013
Published: 07 May 2014
|
|
|
|
[1] |
LAN Peng, TIE Zhan-peng, ZHANG Wei, MIAO Hong-sheng, YAN Qing-zhong, ZHANG Jia-quan. Research progress on spot segregation defects in continuously cast semi-products[J]. Iron and Steel, 2020, 55(2): 11-22. |
[2] |
LIU Lan-xiao, WANG Lin, WU Nai, ZHOU Na, WANG Lun, XU Ke-hao. Cause analysis and improvement measures of white line defect on tinplate surface[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(1): 41-. |
[3] |
MA Hengbao,JIAO Kexin,ZHANG Jianliang,FAN Xiaoyue,CHEN Yanbo,ZHENG Pengchao. Phase composition and properties analysis of slag crust in #br# largesize blast furnace copper stave[J]. Iron and Steel, 2019, 54(6): 20-26. |
[4] |
LI Feng-guang, QI Cheng-lin,YE Si-you,SHI Qiu-yue,GUO Rui, LIU Jian-yong. Experiment on hydrogen-embrittlement-caused failure of copper cooling stave[J]. Iron and Steel, 2019, 54(4): 92-97. |
[5] |
LIU Wen-hua,XU Gang-jun,ZHANG Li-qin. Causes and control measures of corner crack in DC01EK[J]. , 2019, 44(1): 49-53. |
[6] |
ZHANG Zheng-lin, WANG Xiang-hong. Control of longitudinal surface crack of tube steel A29[J]. , 2018, 43(6): 71-73. |
|
|
|
|