Effect and Mechanism of Heat Treatment on Mechanical Property of AM355 Steel |
SUN Yong-qing1, LIANG Jian-xiong1, YANG Zhi-yong1, LIU Zhen-bao1, LI Wen-hui1, ZHANG Li-na2 |
1. Special Steel Institute, Central Iron and Steel Research Institute, Beijing 100081, China 2. Technical Centre, Fushun Special Steel Co., Ltd., Fushun 113001, Liaoning, China |
|
|
Abstract Different heat treatment process on AM355 steel bars were searched, which were produced by VIM+ESR technique and forged into φ80mm. Mechanical properties were tested after different quench temperatures, followed by same deep cold and different temperature. The results show that, with a contrast of traditional heat treatment (1 070 ℃×1 h AC+(-70 ℃)×8 h+200 ℃×2 h AC), new heat treatment process (1 000 ℃×1 h AC+(-70 ℃)×8 h+450 ℃×2 h AC+200 ℃×2 h AC) can lead a rise of about 100 MPa in strength and 5HRC in hardness. Details of mechanical property are: [Rm=]1 630 MPa, [Re=]1 380 MPa, [A=]16%, [Z=]59%, impact energy 51 J, 50HRC. Sorts and precipitations of carbides in this AM355 bar were carried out by SEM and TEM, and strengthening mechanism were also searched. In conclusion, the quenching temperature has main effect on grain size, carbides, remained austenite, etc., and the exist of M23C6 carbide can lead a high strength.
|
Received: 25 November 2013
Published: 10 September 2014
|
|
|
|
|
[1] |
古立新,金建军.回火温度对1CrlSNi4Mo3N钢组织和性能的影响[J][J].材料工程, 2007, 0(1):7-10
|
[1] |
古立新,金建军.回火温度对1CrlSNi4Mo3N钢组织和性能的影响[J][J].材料工程, 2007, 0(1):7-10
|
[2] |
杨晓燕,郭春河.某型机载投放装置锁制机构发生粘着磨损故障分析[J][J].航空兵器, 2008, 0(2):56-58
|
[2] |
杨晓燕,郭春河.某型机载投放装置锁制机构发生粘着磨损故障分析[J][J].航空兵器, 2008, 0(2):56-58
|
[3] |
孙永庆,梁剑雄,杨志勇 等.化学成分和热处理对不锈钢组织和力学性能的影响[J].钢铁, 2011, 48(5):68-70
|
[3] |
孙永庆,梁剑雄,杨志勇 等.化学成分和热处理对不锈钢组织和力学性能的影响[J].钢铁, 2011, 48(5):68-70
|
[4] |
陆世英.不锈钢[M]. 北京: 原子能出版社, 1995:337
|
[4] |
陆世英.不锈钢[M]. 北京: 原子能出版社, 1995:337
|
[5] |
赵振业.合金钢设计[M]. 国防工业出版社, 1999: 264
|
[5] |
赵振业.合金钢设计[M]. 国防工业出版社, 1999: 264
|
|
|
|