Experimental and Mechanism on Pellet-Making of Magnetic Iron Ore Concentrate in Han-Xing Area |
LIU Cheng-song1, LI Jing-she1, YANG Shu-feng1, GAO Xiang-zhou1, MA Bo2 |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China 2. Xingtai Iron and Steel Limited Corporation, Xingtai 054027, Hebei, China |
|
|
Abstract Based on the experiment for pelletizing in production, influence of bentonite proportion, water proportion and damp milling time on green ball properties in pellet-making of a magnetic iron ore concentrate in Han-xing area were investigated, which the optimum conditions were 2.0%, 8.5%-9.0% and 6 min respectively. Moreover, the effect of pre-heating temperature, pre-heating time, roasting temperature and roasting time on consolidation properties of the pellet was studied based on experiments in laboratory and the microstructure of pellet and consolidation mechanism were analyzed by optical microscope. Results show that the suitable pre-heating temperature and time were 880-920 ℃ and 20 min; the suitable roasting temperature and time were 1250 ℃ and 20 min.
|
Received: 19 October 2013
Published: 13 October 2014
|
|
|
|
|
[1] |
赵威,王翠轻.邯邢磁铁矿精粉用作球团矿原料的试验研究[J].烧结球团,2008,33(6):11-13.
|
[1] |
赵威,王翠轻.邯邢磁铁矿精粉用作球团矿原料的试验研究[J].烧结球团,2008,33(6):11-13.
|
[2] |
李建朝,伊凤永,李福民,等.混合铁矿粉的烧结基础特性[J].钢铁,2013,48(5):7-10.
|
[2] |
李建朝,伊凤永,李福民,等.混合铁矿粉的烧结基础特性[J].钢铁,2013,48(5):7-10.
|
[3] |
黄柱成,张元波,陈耀铭,等.以赤铁矿为主配加磁铁矿制备的氧化球团矿显微结构[J].中南工业大学学报(自然科学版),2003,34(6):606-610.
|
[3] |
黄柱成,张元波,陈耀铭,等.以赤铁矿为主配加磁铁矿制备的氧化球团矿显微结构[J].中南工业大学学报(自然科学版),2003,34(6):606-610.
|
[4] |
青格勒,吴铿,屈俊杰,等.不同含镁添加剂对球团矿工艺参数及质量的影响[J].钢铁,2013,48(7):17-22.
|
[4] |
青格勒,吴铿,屈俊杰,等.不同含镁添加剂对球团矿工艺参数及质量的影响[J].钢铁,2013,48(7):17-22.
|
[5] |
唐钰,张勇,储满生,等.高铬型钒钛磁铁矿配量增加对氧化球团质量的影响[J].东北大学学报(自然科学版),2013,34(7):957-960.
|
[5] |
唐钰,张勇,储满生,等.高铬型钒钛磁铁矿配量增加对氧化球团质量的影响[J].东北大学学报(自然科学版),2013,34(7):957-960.
|
[6] |
Nurcan T, Emek M D, Mehmet P. Utilization of pyrite ash wastes by pelletization process[J]. Powder Technology, 2007, 14(176): 72-76.
|
[6] |
Nurcan T, Emek M D, Mehmet P. Utilization of pyrite ash wastes by pelletization process[J]. Powder Technology, 2007, 14(176): 72-76.
|
[7] |
Ishizaki K, Nagata K, Hayashi T. Production of Pig Iron from Magnetite Ore–Coal Composite Pellets by Microwave Heating[J]. ISIJ International, 2006, 46(10): 1403-1409.
|
[7] |
Ishizaki K, Nagata K, Hayashi T. Production of Pig Iron from Magnetite Ore–Coal Composite Pellets by Microwave Heating[J]. ISIJ International, 2006, 46(10): 1403-1409.
|
[8] |
张一敏.球团矿生产技术[M].北京:冶金工业出版社,2005:78-80.
|
[8] |
张一敏.球团矿生产技术[M].北京:冶金工业出版社,2005:78-80.
|
[9] |
秦善.晶体学基础[M].北京:北京大圩出版社,2004:221-224.
|
[9] |
秦善.晶体学基础[M].北京:北京大圩出版社,2004:221-224.
|
[1] |
DU Liang, HAN Xiu-li, ZHANG Quan-sheng, ZHOU Xiang, YANG Hong-da, WANG Ying. Quantitative relation between mineralogical structure and metallurgical properties of sinter of import iron ore[J]. Iron and Steel, 2020, 55(6): 38-45. |
[2] |
YANG Nan,GUO Xing-min. Effect of SiO2 on composition and microstructure of crystal products of CaOFe2O3 melt[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 712-717. |
[3] |
WU Jing- yi,SUN Xin- jun,LI Jian,WANG Xiao- jiang,ZHOU Shi- tong. Effect of heat treatments on interfaces of hot rolled Q235- TA2 clad plate with a niobium interlayer[J]. , 2018, 30(3): 177-184. |
[4] |
REN Pei- dong,WU Xiao- qiang,WANG Chang- bo,HUI Kai,LI Ju- bao. Effect of solution treatment on structure of oxide scales for 2205 duplex stainless steel[J]. , 2018, 30(12): 1006-1012. |
[5] |
LU Hua,WU Sheng-li,ZHANG Jian-liang,CHANG Feng,LI Hong. Forming dynamics of pellet made frozinc-bearing dust in steel plant[J]. Iron and Steel, 2017, 52(5): 5-12. |
[6] |
SONG Tu-shun,, ZHU Li-guan, WANG Xing-juan, XIAO Peng-cheng, WANG Jian-tao. Research of Q345B steel protective slag microstructure and the mineral composition[J]. , 2017, 42(5): 29-32. |
|
|
|
|