Corrosion Resistance Research of Low-Nickel Cr-Mn-N Stainless Steel Containing Rare Earth Element La |
ZHAO Li-ping, QIN Xiang-dou, ZHANG Hui-min, HE Jian-xin |
College of Material and Metallurgy Engineering, Inner Mongolia University of Science and Technology, Baotou 014010, Nei Mongol, China |
|
|
Abstract Low-nickel Cr-Mn-N stainless steel with different content of rare earth La element was the research object, and the electrochemical behavior was studied by electrochemical impedance spectrum and polarization curve in the cyclic immersion corrosion environment. The experimental result shows that rare earth element La can affect the electrode potential of Low-nickel Cr-Mn-N stainless steel. When the content of La element was in the range of 0-0.014%, the amount of rare earth to be added was more, the substrate electrode potential of the stainless steel was higher. When Low-nickel Cr-Mn-N stainless steel contained the 0.004 9% of La element, the corrosion resistance was best in 3.5% NaCl solution for 48 days of simulation of atmospheric corrosion, but the content of La element exceeded a certain range, the corrosion resistance decreased.
|
Received: 03 January 2014
Published: 13 October 2014
|
|
|
|
[1] |
袁琳,高原,张维. 201不锈钢离子渗氮和离子镀TiN复合强化层的耐蚀性[J].材料热处理学报,2011(10):144-147.
|
[1] |
袁琳,高原,张维. 201不锈钢离子渗氮和离子镀TiN复合强化层的耐蚀性[J].材料热处理学报,2011(10):144-147.
|
[2] |
张慧敏,崔朝宇,赵莉萍.镧对4Cr13钢组织及耐蚀性的影响[J].中国稀土学报,2011(2):100-104.
|
[2] |
张慧敏,崔朝宇,赵莉萍.镧对4Cr13钢组织及耐蚀性的影响[J].中国稀土学报,2011(2):100-104.
|
[3] |
Z.X.Zhang,G.Lin,Z.Xu. Effects of light pre-deformation on pitting corrosion resistance of copper-bearing ferrite antibacterial stainless steel[J]. journal of materials processing technology,205(2008):419–424.
|
[3] |
Z.X.Zhang,G.Lin,Z.Xu. Effects of light pre-deformation on pitting corrosion resistance of copper-bearing ferrite antibacterial stainless steel[J]. journal of materials processing technology,205(2008):419–424.
|
[4] |
曹楚南. 腐蚀电化学原理[M]. 第三版, 北京: 化学工业出版社, 2008: 203-215.
|
[4] |
曹楚南. 腐蚀电化学原理[M]. 第三版, 北京: 化学工业出版社, 2008: 203-215.
|
[5] |
H. Wang, M.P.Brady, K.L.More, H.M.MeyerIII, John A.Turner. Thermally nitrided stainless steels for polymer electrolyte membrane fuel cell bipolar plates[J]. Journal of Power Sources,138(2004):79–85.
|
[5] |
H. Wang, M.P.Brady, K.L.More, H.M.MeyerIII, John A.Turner. Thermally nitrided stainless steels for polymer electrolyte membrane fuel cell bipolar plates[J]. Journal of Power Sources,138(2004):79–85.
|
[6] |
付燕,林昌健,蔡文达.微电化学技术研究双相不锈钢优选腐蚀行为[J].金属学报,2005(3):302-306.
|
[6] |
付燕,林昌健,蔡文达.微电化学技术研究双相不锈钢优选腐蚀行为[J].金属学报,2005(3):302-306.
|
|
|
|