Effects of Manganese Content and Finishing Rolling Temperature on the Microstructure and Mechanical Properties of Low Cost Middle Titanium Q345B Steel |
YANG Cai-shui1, LUO Xu1,2, LI Jun-hong2, KANG Yong-lin1 |
(1. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083,China 2. Panzhihua Iron and Steel Research Institute, Panzhihua 617000, Sichuan, China) |
|
|
Abstract Influences of different manganese content (0.6%-1.0%) and finishing rolling temperature on the microstructure and mechanical properties of low cost middle titanium (0.04%-0.05%) Q345B Steels were studied by laboratory rolling experiments, combining TEM observing the rule of Ti precipitation in the steel. The results indicate that when the manganese content was 0.8% and the finish rolling temperature was 850 ℃, the yield strength of the experimental steel was 491 MPa, the tensile strength was 625 MPa and the elongation was 33.6%. It can reduce the cost to maximum under the condition of meeting mechanical properties. The precipitation of Ti is mainly spherical nanometer size TiC particles, with a small amount of square large TiN particles.
|
Received: 17 March 2014
Published: 02 November 2014
|
|
|
|
|
[1] |
李婧, 赵德文, 刘相华, 等.低成本钢高强度厚板的开发[J].机械工程材料, 2009, 33(10):68-71
|
[1] |
李婧, 赵德文, 刘相华, 等.低成本钢高强度厚板的开发[J].机械工程材料, 2009, 33(10):68-71
|
[2] |
牛见青, 刘东升.低成本系列厚钢板的控轧控冷工艺[J].上海金属, 2013, 35(2):36-40
|
[2] |
牛见青, 刘东升.低成本系列厚钢板的控轧控冷工艺[J].上海金属, 2013, 35(2):36-40
|
[3] |
LI L, DING H, DU L, et al.Influence of Mn content and hot deformation on transformation behavior of C-Mn steels[J].Journal of Iron and Steel Research, International, 2008, 15(2):51-55
|
[3] |
LI L, DING H, DU L, et al.Influence of Mn content and hot deformation on transformation behavior of C-Mn steels[J].Journal of Iron and Steel Research, International, 2008, 15(2):51-55
|
[4] |
Byun J S, Shim J H, Cho Y W.Influence of Mn on microstructural evolution in Ti-killed C–Mn steel[J].Scripta Materialia, 2003, 48(4):449-454
|
[4] |
Byun J S, Shim J H, Cho Y W.Influence of Mn on microstructural evolution in Ti-killed C–Mn steel[J].Scripta Materialia, 2003, 48(4):449-454
|
[5] |
谢利群, 毛新平, 霍向东.Ti对钢的组织性能的影响[J].冶金丛刊, 2005, 155(1):1-4
|
[5] |
谢利群, 毛新平, 霍向东.Ti对钢的组织性能的影响[J].冶金丛刊, 2005, 155(1):1-4
|
[6] |
Wang Z, Mao X, Yang Z, et al.Strain-induced precipitation in a Ti micro-alloyed HSLA steel[J].Materials Science and Engineering: A, 2011, 529:459-467
|
[6] |
Wang Z, Mao X, Yang Z, et al.Strain-induced precipitation in a Ti micro-alloyed HSLA steel[J].Materials Science and Engineering: A, 2011, 529:459-467
|
[7] |
干勇, 田志凌.钢铁材料手册(上)[M]. 北京: 化学工业出版社, 2009.
|
[7] |
干勇, 田志凌.钢铁材料手册(上)[M]. 北京: 化学工业出版社, 2009.
|
[8] |
郑晓飞, 康永林, 孟德亮, 等.终轧温度对抗大变形管线钢组织性能的影响[J].北京科技大学学报, 2011, 33(5):557-562
|
[8] |
郑晓飞, 康永林, 孟德亮, 等.终轧温度对抗大变形管线钢组织性能的影响[J].北京科技大学学报, 2011, 33(5):557-562
|
[9] |
周建, 康永林, 毛新平, 等.对高强耐候钢力学性能的影响[J].北京科技大学学报, 2006, 28(10):926-930
|
[9] |
周建, 康永林, 毛新平, 等.对高强耐候钢力学性能的影响[J].北京科技大学学报, 2006, 28(10):926-930
|
[1] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
[2] |
CAO Yan-guang, LI Zhao-dong, DING Can-can, ZHANG Jin-wen, YONG Qi-long, GAO Jian-bing. Effect of niobium addition on hardenability of high-speed railway axle steel[J]. Iron and Steel, 2020, 55(6): 107-112. |
[3] |
HE Ya-yuan,LI Li-wei,YIN Yun-yang,DENG Zhao-jun. Evolution of microstructure and properties of thickness section of wearresistant steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 512-518. |
[4] |
LI Lan-xin1,WANG Min1,JUAN Rong-fei1,BAO Yan-ping1,YANG Jin2. Distribution characteristics of oxides and sulfide inclusions in key areas of gear steel forgings[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 370-376. |
[5] |
ZENG Ze-yun, LI Chang-rong, LI Zhi-ying, LIU Zhan-lin,LI Zheng-song, ZHAI Yong-qiang. Thermodynamic analysis of titanium precipitation in HRB500E seismic steel[J]. Iron and Steel, 2020, 55(5): 45-51. |
[6] |
ZHAO Yun-peng, YU Chao, XIAO Hong, WU Zong-he, XU Peng-peng, XIE Hong-biao. Effect of pure iron interlayer on mechanical properties of hot rolled stainless steel clad plate[J]. Iron and Steel, 2020, 55(5): 73-79. |
|
|
|
|