Application of Brown Coal-Based Hyper Coal in Coal Blending for Coking |
FAN Li-hua1, WANG Lei1,2,3, HOU Cai-xia1, YIN Jia-nan1, LIANG Ying-hua1 |
1. College of Chemical Engineering, Hebei United University, Tangshan, 063009 2. Wulanchabu ENN Coal Gasification Minning Technology Co., Wulanchabu 012000, Nei Mongol, China 3. State Key Laboratory of Coal-Based Low Carbon Energy, Hebei United University, Langfang, 065001, Hebei, China) |
|
|
Abstract The hyper coal was high-temperature extracted under the condition of using N-methyl pyrrolidone and wash oil as the solvents respectively. The prepared hyper coal was characterized by means of FT-IR, 13C CP/MAS NMR and thermogravimetric analysis. Compared with the raw coal, hyper coal had lower oxygen content and higher heat value with N-methyl pyrrolidone or wash oil as solvent and more aromatic components with wash oil as solvent. Hyper coal can be applied in coal blending for coking. When it was added with the proportion of 10%, the softening point decreased by 70 -80 ℃, and the plasticity range of paste increased. The coke reactivity decreased about 1 percentage point, and the post-reaction strength was increased about 3.6 percentage points.
|
Received: 24 March 2014
Published: 02 November 2014
|
|
|
|
[1] |
DU Yun-cong1,YI Yuan-rong1,2,3,BAI Shu-qi1,MA Zhong-le1,FANG Ming-hang1,MA Wen-qing1. Change of Ca occurrence state in carbonation process of LF refining slag[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(3): 195-203. |
[2] |
SHI Zhi-yue1, XU Hai-feng1, XU Da1, YU Feng1, WANG Chang2, CAO Wen-quan1. Characterization of inclusions in GCr15 bearing steel by ASPEX and rotary bending fatigue methods[J]. Iron and Steel, 2019, 54(4): 55-62. |
[3] |
WANG Hai-yang,ZHANG Jian-liang,WANG Guang-wei,LIU Si-yuan,LIN Hao,XU Run-sheng. Feasibility research of brown coal injection for blast furnace[J]. Chinese Journal of Iron and Steel, 2017, 29(1): 39-43. |
[4] |
SHEN Wei,GAO Jia-qiang. Characterization technique of microcosmic inclusions in clean steel and its application[J]. Chinese Journal of Iron and Steel, 2016, 34(4): 1-6. |
[5] |
SUN Yi-qiang,CHEN Xue-yan,ZHANG Ping,ZHOU Yong. Analysis and discussion on the sorbite volume fraction measurement method of 72A steel wire rod[J]. Chinese Journal of Iron and Steel, 2015, 33(5): 25-28. |
[6] |
qing-gong LV Cheng-Ming LI ai-juan NI. Quantitative Study on the Non-{111} Textures of Micro-carbon Deep Drawing Steel Sheet[J]. Chinese Journal of Iron and Steel, 2010, 22(04): 52-52. |
|
|
|
|