Effects of boron on hardenability and mechanical properties of 60 mm Q690D steel |
YANG Wei-yu1,DONG Rui-feng2, GAO Feng1,LI Zhi-li1 |
(1. Technical Center, Steel Union Co., Ltd., Baotou Steel Group Corporation, Baotou 014010, Nei Mongol, China 2. School of Materials Science and Engineering, Inner Mongolia University of Technology, Hohhot 010051, Nei Mongol, China) |
|
|
Abstract By jominy test, [Z] direction hardness test, microstructure and mechanical properties analysis,the effects of boron on hardenability and mechanical properties of 60 mm Q690D steel were studied. The results show that the trace solution boron can significantly improve the hardenability of 60 mm Q690D steel; compared with the experimental steel without boron addition,quenching microstructure of experimental steel with boron addition was transformed from martensite/bainite complex phases to lath martensite at thickness of 1/4, the maximum hardness difference of [Z] direction at transverse section for quenching was reduced from 9HRC to 4HRC and that for tempering was reduced from 5HRC to 3HRC, which made the homogeneity of hardness at [Z] direction improved, as well as the strength and toughness for quenching and tempering of experimental steel with boron.
|
Received: 06 June 2014
Published: 02 February 2015
|
|
|
|
[1] |
M.V.Bobylev. Control of the Quality of Boron-bearing Steel for the Production of High-strength fasteners[J]. Metal Science and Heat Treatment, 2001, 43 (11-12): 445.
|
[1] |
M.V.Bobylev. Control of the Quality of Boron-bearing Steel for the Production of High-strength fasteners[J]. Metal Science and Heat Treatment, 2001, 43 (11-12): 445.
|
[2] |
D.V.Ovchinnikov,O.A.Sofrygina, S.Yu.Zhukova, etc.. Influence of Microalloying with Boron on the Structure and Properties of High-Strength Oil Pipe[J]. Steel in Translation, 2011, 41(4): 356-360.
|
[2] |
D.V.Ovchinnikov,O.A.Sofrygina, S.Yu.Zhukova, etc.. Influence of Microalloying with Boron on the Structure and Properties of High-Strength Oil Pipe[J]. Steel in Translation, 2011, 41(4): 356-360.
|
[3] |
T.I.Titova, N.A.Shulgan, I.Yu,etc.. Effect of Boron Microallying on the Structure and Hardenability of Building Steel [J]. Metal Science and Heat Treatment, 2007, 49(1-2):39-44.
|
[3] |
T.I.Titova, N.A.Shulgan, I.Yu,etc.. Effect of Boron Microallying on the Structure and Hardenability of Building Steel [J]. Metal Science and Heat Treatment, 2007, 49(1-2):39-44.
|
[4] |
杨俊,肖强健,李玉路,等.50mm厚高强度低合金钢Q550D的成分优化[J].钢铁,2012,47(12):55-58.
|
[4] |
杨俊,肖强健,李玉路,等.50mm厚高强度低合金钢Q550D的成分优化[J].钢铁,2012,47(12):55-58.
|
[5] |
唐郑磊,许少普,崔冠军,等.110mm厚高强度结构钢Q690D-Z35的研发[J]. 钢铁研究,2012,40(2):41-43.
|
[5] |
唐郑磊,许少普,崔冠军,等.110mm厚高强度结构钢Q690D-Z35的研发[J]. 钢铁研究,2012,40(2):41-43.
|
[6] |
段承轶,詹卢刚. 调质工艺对Q690D钢综合力学性能及组织的影响[J]. 钢铁研究学报,2013,25(2):48-53.
|
[6] |
段承轶,詹卢刚. 调质工艺对Q690D钢综合力学性能及组织的影响[J]. 钢铁研究学报,2013,25(2):48-53.
|
[7] |
A. A. Azarkevich, L. V. Kovalenko, V. M. Krasnopoiskii. The Optimum Content of Boron in Steel[J]. Metal Science and Heat Treatment, 1995,37(1-2):22-24.
|
[7] |
A. A. Azarkevich, L. V. Kovalenko, V. M. Krasnopoiskii. The Optimum Content of Boron in Steel[J]. Metal Science and Heat Treatment, 1995,37(1-2):22-24.
|
[8] |
V. I. Zhuchkov, A. A. Akberdin, N. A. Vatolin, etc.. Application of Boron-Containing Materials in Metallurgy[J]. Manufacture of Ferroalloys,2011,2011(12):1134-1137.
|
[8] |
V. I. Zhuchkov, A. A. Akberdin, N. A. Vatolin, etc.. Application of Boron-Containing Materials in Metallurgy[J]. Manufacture of Ferroalloys,2011,2011(12):1134-1137.
|
[9] |
Sangeeta Khare, Kyooyoung Leeb, H. K. D. H.,etc.. Relative effects of Mo and B on ferrite and bainite kinetics in strong steels[J]. International Journal of Materials Research, 2009, 100: 1513-1520.
|
[9] |
Sangeeta Khare, Kyooyoung Leeb, H. K. D. H.,etc.. Relative effects of Mo and B on ferrite and bainite kinetics in strong steels[J]. International Journal of Materials Research, 2009, 100: 1513-1520.
|
[10] |
A. P. Rychkov,K. A. Lanskaya. Effect of Combined Additions of Boron and Rem on the Properties of Steel [J]. Metal Science and Heat Treatment, 1978,20(2):149-151.
|
[10] |
A. P. Rychkov,K. A. Lanskaya. Effect of Combined Additions of Boron and Rem on the Properties of Steel [J]. Metal Science and Heat Treatment, 1978,20(2):149-151.
|
[11] |
C. A. Suski,C. A. S. Oliveira. Effect of Austenitization Temperature on the Precipitation of Carbides in Quenched Low Carbon Boron Steel[J]. Metallogr. Microstruct. Anal. ,2013, 2:79–87.
|
[11] |
C. A. Suski,C. A. S. Oliveira. Effect of Austenitization Temperature on the Precipitation of Carbides in Quenched Low Carbon Boron Steel[J]. Metallogr. Microstruct. Anal. ,2013, 2:79–87.
|
[12] |
M. V. Bobylev. Control of the Quality of Boron-bearing Steels for the Production of High-strength Fasteners[J]. Metal Science and Heat Treatment,2001,43(11-12):445.
|
[12] |
M. V. Bobylev. Control of the Quality of Boron-bearing Steels for the Production of High-strength Fasteners[J]. Metal Science and Heat Treatment,2001,43(11-12):445.
|
[1] |
Jun Zhao, Hai-bin Zuo, Chao Ling, Wen-tao Guo, Jing-song Wang, Qing-guo Xue. Microstructure evolution of coke under CO<sub>2</sub> andH<sub>2</sub>O atmospheres[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(7): 743-754. |
[2] |
Xiao‑hui Chen, Bo Chen, Xu Cheng, Guo‑chao Li, Zheng Huang. Microstructure and properties of hybrid additive manufacturing 316L component by directed energy deposition and laser remelting[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(7): 842-848. |
[3] |
Wan‑lin Wang, Guo‑min Ying, Jie Zeng, Hai‑hui Zhang. Effect of electropulsing treatment on solidification behavior of spring steels in a continuous casting mold simulator[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(6): 656-664. |
[4] |
Chun‑xu Wang, Yuan‑hang Gao, Yong Li, Shun Han, Shao‑zun Liu, Peng‑jie Zhang. Effects of solid-solution temperature on microstructure and mechanical properties of a novel 2000 MPa grade ultra-high-strength steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(6): 710-718. |
[5] |
Xiao-ping Ma, Dian-zhong Li. Coalescence-dominated microstructure evolution during solidification of 20SiMn steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(5): 506-516. |
[6] |
Ming Lei, Wei‑jun Hui, Jiao‑jiao Wang, Yong‑jian Zhang, Xiao‑li Zhao. Microstructure and mechanical properties of hot-rolled V-microalloyed Al-containing medium-Mn steel[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2020, 27(5): 537-548. |
|
|
|
|