Liquid generation capabilities of Chengde vanadium-titanium magnetite during sintering |
Lü Qing1, HUANG Hong-hu1, WAN Xin-yu1, LIU Xiao-jie2, QIE Ya-na1, DING Hai-chao1 |
(1. School of Metallurgy and Energy, Hebei United University, Tangshan 063009, Hebei, China 2. School of Materials and Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China) |
|
|
Abstract The base properties of vanadium-titanium magnetite sintered were studied by TSJ-3 Micro sintering machine and then the influences of alkalinity,temperature and calcination atmosphere on the vanadium-titanium magnetite phase formation and the solid phase material were also analyzed by FactSage6.3.The results indicated that the sintering temperature has a great impact on the liquid content. With the increase of sintering temperature,the liquid phase was gradually increased,but material layer with different heights also leads to slightly different liquid content. Monotonicity was found between alkalinity and liquid volume and the alkalinity increased with the increase of liquid phase. With the gradual increase of the oxidizing atmosphere,liquid content is increased,but the growth rate is slow. While with too much oxygen injected,liquid content will be reduced. By comparing the results of software simulation and actual sintering,the results of sintering test were basically consistent with the theoretical calculations.
|
Received: 30 April 2014
Published: 18 March 2015
|
|
|
|
|
[1] |
MA Li-ming,ZHANG Jian-liang,WU Sheng-li,LIU Zheng-jian,WANG Yao-zu,XU Chen-yang. Treatment of vanadiumtitanium magnetite based on fluxed green ball composite agglomeration process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 462-469. |
[2] |
HE Zhan-wei, XUE Xiang-xin. Basic sintering characteristics of several typical vanadium titanium magnetite[J]. Iron and Steel, 2020, 55(5): 20-25. |
[3] |
CHU Man-sheng,TANG Jue,LIU Zheng-gen,YING Zi-wei. Present situation and progress of comprehensive utilization for high-chromium vanadium-bearing titanomagnetie[J]. Chinese Journal of Iron and Steel, 2017, 29(5): 335-344. |
[4] |
WANG Yao-zu,ZHANG Jian-liang,LIU Zheng-jian,ZHANG Ya-peng,LIU Dong-hui,DU Cheng-bo. Effects of[w(TiO2)]on mineral structure and softening-melting property of sinter[J]. Iron and Steel, 2017, 52(3): 20-28. |
[5] |
HONG Lu-kuo,QI Yuan-hong,SUN Cai-jiao,GAO Jian-jun,WU Bing-qiang. Direct reduction of coal based vanadium-bearing titanomagnetite[J]. Iron and Steel, 2017, 52(11): 15-19. |
[6] |
WANG Yao-zu,ZHANG Jian-liang,LIU Zheng-jian,ZHANG Ya-peng,LIU Dong-hui,DU Cheng-bo. Effects of[w(TiO2)]on mineral structure and softening-melting property of sinter[J]. Iron and Steel, 2017, 52(10): 20-28. |
|
|
|
|