Application of CO2 in BOF |
WAN Xue-feng,CAO Dong,LIU Xiang,ZHU Xiao-lei,LIAO Xiang-wei |
Iron and Steel Academe of Ansteel Group, Anshan 114009, Liaoning, China |
|
|
Abstract By the thermodynamic analysis of top blowing CO2 in the converter, combined with laboratory simulation result of top blowing O2+CO2 mixture gas in converter, some key parameters of CO2 used in converter were established. It is concluded that although pure CO2 injected in the converter could achieve decarburize, the drop of temperature was rather large. When the CO2 supplying intensity was 3.0 m3/(t·min), the reduction of temperature was 15.1 ℃/min; By blowing O2+CO2 mixture gas, temperature balance could be realized, but the largest theoretical proportion of CO2 in mixture gas was 79.1%; with the increase of CO2 proportion, the carbon and oxygen product of molten steel at the blowing end was reduced, under the condition of [φ(CO2)∶][φ(O2)=1][∶]1, the carbon and oxygen product could be controlled in the range of (25~32)×10-8.
|
Received: 06 May 2014
Published: 28 April 2015
|
|
|
|
[1] |
朱荣.应用COMI炼钢工艺控制炼钢烟尘内循环的研究[J].冶金能源, 2010, 29(1):48-51
|
[1] |
朱荣.应用COMI炼钢工艺控制炼钢烟尘内循环的研究[J].冶金能源, 2010, 29(1):48-51
|
[2] |
宁晓钧.利用CO2减少炼钢烟尘的实验研究[J].炼钢, 2009, 25(5):32-34
|
[2] |
宁晓钧.利用CO2减少炼钢烟尘的实验研究[J].炼钢, 2009, 25(5):32-34
|
[3] |
易操.基于30t转炉的COMI炼钢工艺实验研究[J].过程工程学报, 2009, 9(增1):222-225
|
[3] |
易操.基于30t转炉的COMI炼钢工艺实验研究[J].过程工程学报, 2009, 9(增1):222-225
|
[4] |
靳任杰.二氧化碳一氧气混合喷吹炼钢的初步研究[J].冶金研究, 2007, :125-128
|
[4] |
靳任杰.二氧化碳一氧气混合喷吹炼钢的初步研究[J].冶金研究, 2007, :125-128
|
[5] |
吕 明.应用COMI炼钢工艺控制转炉脱磷基础研究[J].钢铁, 2011, 46(8):31-35
|
[5] |
吕 明.应用COMI炼钢工艺控制转炉脱磷基础研究[J].钢铁, 2011, 46(8):31-35
|
[6] |
张慧书.直流钢包炉中空电极喷吹Ar-CO2对钢水温度的影响[J].工业炉, 2009, 31(5):1-4
|
[6] |
张慧书.直流钢包炉中空电极喷吹Ar-CO2对钢水温度的影响[J].工业炉, 2009, 31(5):1-4
|
[1] |
LI Lin, LI Ming-ming, LI Qiang, ZOU Zong-shu. Melt splashing behavior of steelmaking converter with nozzle-twisted lance[J]. Iron and Steel, 2020, 55(6): 54-60. |
[2] |
YANG Li-bin, ZENG Jia-qing, DENG Yong, XU Xiao-wei, WU Li-ping. Highly efficiency and long-life combined blowing technology of big converter[J]. Iron and Steel, 2020, 55(4): 45-52. |
[3] |
DONG Wen-liang, PAN Hong-wei, LUO Lei, JI Chen-xi, LI Hai-bo, TIAN Zhi-hong. Phosphorous distribution in dephosphorization slag[J]. Iron and Steel, 2020, 55(2): 75-81. |
[4] |
ZHOU Zhenyu, TANG Ping, ZHOU Zunchuan, HOU Zibing, WEN Guanghua. Optimization on nozzle parameters of 200 t combined blowing vanadium extraction converter[J]. Iron and Steel, 2019, 54(9): 50-56. |
[5] |
Guang-sheng Wei, Rong Zhu, Yun Wang, Xue-tao Wu, Kai Dong. Technological innovations of electric arc furnace bottom-blowing in China[J]. JOURNAL OF IRON AND STEEL RESEARCH,INTERNATIONAL, 2019, 26(9): 909-916. |
[6] |
WANG Linzhu,BAO Yanping,LI Xiang. Comparison of twostage dephosphorization during remaining #br# slagdouble slag process in converter[J]. Iron and Steel, 2019, 54(8): 37-42. |
|
|
|
|