Optimal proportion of Ti, Mg and Al in BF slag |
ZHANG Xu-sheng1,Lü Qing1,LIU Xiao-jie2,LIU Zhao-qing1,LA Xiao-shuai1,QIE Ya-na1 |
1. Key Laboratory for Advanced Metallurgy Technology, Ministry of Education, North China University of Science and Technology, Tangshan 063009, Hebei, China 2. School of Materials and Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China |
|
|
Abstract According to the spot slag of Chenggang, the influence of Ti, Mg and Al on properties, such as viscosity, melting temperature and desulfurization were investigated. The results show that Ti, Mg and Al had a large effect on the properties of slag in the CaO-Al2O3-SiO2-MgO-TiO2 slag system. With the content of MgO increasing, melting temperature decreased and then rised, viscosity decreased and desulfurization rised and then decreased. With the content of Al2O3 increasing, melting temperature rised and then decreased, the change of viscosity was complicated and desulfurization decreased. With the content of TiO2 increasing, melting temperature and viscosity tended to rise, and desulfurization was decreased. When the basicity of slag was 1.12, the suitable slag composition was that the content of MgO was about 13.95%, the content of Al2O3 was about 13.75%, the content of TiO2 was below 10.57%. The ratio of Ti, Mg and Al in slag is reasonable controlled, which is conducive to perfecting the property of slag and improving the production of blast furnace.
|
Received: 09 June 2014
Published: 11 June 2015
|
|
|
|
|
[1] |
王竹民,吕庆,李福民,等. 邯钢高炉渣的熔化性能[J]. 钢铁研究学报,2009,21(5):59-62.
|
[1] |
王竹民,吕庆,李福民,等. 邯钢高炉渣的熔化性能[J]. 钢铁研究学报,2009,21(5):59-62.
|
[2] |
王艺慈,那树人,陈春元,等. 提高包钢炉渣脱硫能力的实验研究[J]. 包头钢铁学院学报,2001,20(2):104.
|
[2] |
王艺慈,那树人,陈春元,等. 提高包钢炉渣脱硫能力的实验研究[J]. 包头钢铁学院学报,2001,20(2):104.
|
[3] |
郭兴忠,李劲明,文光远,等. 中钛型高炉渣的冶金性能[J]. 钢铁钒钛,2000,21(1):1-6.
|
[3] |
郭兴忠,李劲明,文光远,等. 中钛型高炉渣的冶金性能[J]. 钢铁钒钛,2000,21(1):1-6.
|
[4] |
王成立,吕庆,顾林娜,等. 高炉含碱金属氧化物炉渣性能的试验研究[J]. 东北大学学报:自然科学版,2006,27(1):45 -48.
|
[4] |
王成立,吕庆,顾林娜,等. 高炉含碱金属氧化物炉渣性能的试验研究[J]. 东北大学学报:自然科学版,2006,27(1):45 -48.
|
[5] |
张丙怀,,刁岳川,廖东海,等. 富三氧化二铝高炉渣的流动性[J]. 钢铁研究学报, 2005,17(4):14-16.
|
[5] |
张丙怀,,刁岳川,廖东海,等. 富三氧化二铝高炉渣的流动性[J]. 钢铁研究学报, 2005,17(4):14-16.
|
[6] |
万新,裴鹤年,白晨光,等. 钛氧化物还原与钛渣变稠[J]. 重庆大学学报:自然科学版,2000,23(5):36 -39.
|
[6] |
万新,裴鹤年,白晨光,等. 钛氧化物还原与钛渣变稠[J]. 重庆大学学报:自然科学版,2000,23(5):36 -39.
|
[7] |
张淑会,穆红旺,孙艳芹,等. 高铝中钛高炉渣脱硫的动力学机制[J]. 钢铁,2012,47(8):13-16.
|
[7] |
张淑会,穆红旺,孙艳芹,等. 高铝中钛高炉渣脱硫的动力学机制[J]. 钢铁,2012,47(8):13-16.
|
[8] |
张振峰,吕庆,高峰,等. 高TiO2、Al2O3炉渣脱硫能力的试验研究[J]. 钢铁,2008,43(2):14-17.
|
[8] |
张振峰,吕庆,高峰,等. 高TiO2、Al2O3炉渣脱硫能力的试验研究[J]. 钢铁,2008,43(2):14-17.
|
[9] |
张振峰,吕庆,李福民. 高Al2O3钒钛炉渣熔化性能的试验研究[J]. 东北大学学报(自然科学版),2007,28(10):1414-1416.
|
[9] |
张振峰,吕庆,李福民. 高Al2O3钒钛炉渣熔化性能的试验研究[J]. 东北大学学报(自然科学版),2007,28(10):1414-1416.
|
[10] |
王筱留. 钢铁冶金学(炼铁部分)[M]. 北京:冶金工业出版社,1991.
|
[10] |
王筱留. 钢铁冶金学(炼铁部分)[M]. 北京:冶金工业出版社,1991.
|
[1] |
ZHANG Wei-li1,WU Sheng-li1,HU Zhong-jie1,2. Statistical analysis of factors affecting desulfurization rate of activated coke for sintering flue gas[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 281-288. |
[2] |
YIN Chuan-lei, YANG Li-mei, TIAN Chun-yang, MA Jian-chao. Analysis of KR hot metal desulfurizer escaped and slag agglomeration in agitator[J]. Iron and Steel, 2020, 55(1): 34-37. |
[3] |
LU Yanan,WU Shengli,WANG Laixin,KOU Mingyin. Analysis of chemical compositions of slag affecting #br#
desulphurization in hot metal of COREX process[J]. Iron and Steel, 2019, 54(9): 33-38. |
[4] |
LIU Zhe,WANG Yi-ci,ZHAO Feng-guang,LUO Guo-ping,ZHAO Bin. Influence of binary basicity on physical properties of blast furnace slag of Baogang Group[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 696-701. |
[5] |
ZHOU Zhenyu, TANG Ping, HOU Zibing, WEN Guanghua. Effect of w(SiO2)/w(V2O3) on melting and viscosity properties of vanadium slag[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(5): 446-451. |
[6] |
LI Qiu-han1,2, JIA Ya-nan1,2, ZHANG Chao-jie1,2, CHEN Bin1,2, GUO Zi-feng1,2, GUO Jia1,2. Viscosity-structure analysis of CaO-SiO2-MgO-Al2O3-Cr2O3 slags and application of Iida model[J]. Iron and Steel, 2019, 54(4): 99-105. |
|
|
|
|