Evolution of inclusions in non- oriented silicon steel W800 during production process |
PENG Qi- chun1,QIU Lei1,ZOU Jian1,PENG Ming- yao2,ZHANG Liang- zhou2,ZHOU Jian- feng2 |
1.Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education,Wuhan University of Science and Technology,Wuhan 430081,Hubei,China 2.Lianyuan Iron and Steel Corporation of Hualing Group,Loudi 417009,Hunan,China |
|
|
Abstract The cleanliness of steel and the amount,size distribution and morphology of inclusions in non- oriented silicon steel W800,which was produced by 210 t BOF- RH- CC,were studied by oxygen and nitrogen analyzer,scan electron microscopy(SEM),image analytical,bulk sample electrolysis.The results show that w(T[O]) generally decreases, w([N]) increases gradually in steel;the size of most inclusions in the steel is 0- 3 μm,the number of inclusions decreases ceaselessly during the smelting process. The inclusions during RH refining process are Al2O3 and a small amount of MgO- Al2O3. In tundish the number ofMgO- Al2O3 increases,individual inclusion of Al2O3 decreases. The main inclusions in casting slab are AlN,Al2O3 and MnS and the size is blow 10 μm,and individual Al2O3 is not be found,large inclusions mainly are Al2O3- SiO2,CaO- Al2O3- SiO2,CaO- MgO- Al2O3 formed with deoxidation products,slag and lining by the reaction.
|
Received: 14 October 2014
Published: 18 August 2015
|
|
|
|
[1] |
HOU Xin-mei, LIU Yun-song, WANG En-hui. Effect of ladle-lining refractory on non-metallic inclusions in steel[J]. Iron and Steel, 2020, 55(6): 15-24. |
[2] |
YU Hui-xiang, PAN Ming, YANG De-xin. Behavior of inclusions in ultra-low carbon IF steel during deoxidation and alloying process[J]. Iron and Steel, 2020, 55(6): 46-53. |
[3] |
NIU Kai-jun, YANG Wen, ZHANG Li-feng, CHU Yan-ping, ZHANG Hong-qi, GUO Zi-qiang. Thermodynamics and industrial practice of formation of inclusions during solidification of tire cord steels[J]. Iron and Steel, 2020, 55(6): 61-67. |
[4] |
YAN Xue-qiang1,2,ZHENG Wan1,2,WANG Guo-wei1,2,YAN Wen1,LI Guang-qiang1,2. Effect of microporous MgO refractories on steel cleanliness[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 483-490. |
[5] |
LI Lan-xin1,WANG Min1,JUAN Rong-fei1,BAO Yan-ping1,YANG Jin2. Distribution characteristics of oxides and sulfide inclusions in key areas of gear steel forgings[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 370-376. |
[6] |
LI Xiao-yuan,SHI Jie. Ballistic behavior of high strength steel targets during high speed impact of projectile[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 429-436. |
|
|
|
|