Generation mechanism and control strategy of equally- spaced longitudinal stripes on the surface of hot- rolled plate |
YU Yang1,WANG Lin1,ZHANG Xi- bang1,WANG Chang1,CHEN Jin2,JIAO Hui- li2 |
(1. Sheet Metal Research Institute,Shougang Research Institute of Technology,Beijing 100043,China 2. Technology and Quality Division,Shougang Qian’an Steel Company,Qian’an 064404,Hebei,China) |
|
|
Abstract Equally- spaced longitudinal stripes introduced in hot rolling process couldn’t be completely eliminated after pickling,cold rolling and continuous annealing,which seriously affect the quality of finished product. Defect evolution research during the whole process and technological experiment have been carried out,which confirmed that the translations of grinding spiral lines,closely related to the roll grinding process and CVC roll profile curvature,from the finishing work roll surface in last pass to the steel strip surface,was the main cause. Grinding spiral lines on roll surface and the resulting equally- spaced longitudinal strips in hot- rolled sheet surface were caused by the mismatch of grinding wheel surface and the roll surface curve,and could be completely eliminated by optimizing CVC profile of finishing work roll and roll grinding parameters.
|
Received: 25 November 2014
Published: 18 August 2015
|
|
|
|
[1] |
郭太雄, 钟声, 贾斌, 等.冷轧薄板表面条痕缺陷成因及预防[J]. [J].轧钢, 2000, ( (6): ):22-24.-
|
[1] |
郭太雄, 钟声, 贾斌, 等.冷轧薄板表面条痕缺陷成因及预防[J]. [J].轧钢, 2000, ( (6): ):22-24.-
|
[2] |
魏亚彬, 屈明友, 郭艳花.高压水除鳞技术在邯钢生产线上的应用[J].轧钢, 2008, 25(1):59-61
|
[2] |
魏亚彬, 屈明友, 郭艳花.高压水除鳞技术在邯钢生产线上的应用[J].轧钢, 2008, 25(1):59-61
|
[3] |
韩清刚.热轧带钢粗轧高压水除鳞系统数值计算[J].轧钢, 2010, 27(2):40-43
|
[3] |
韩清刚.热轧带钢粗轧高压水除鳞系统数值计算[J].轧钢, 2010, 27(2):40-43
|
[4] |
邱雪松, 谭佳梅, 张永锟, 等.热轧酸洗板表面黑色条纹缺陷成因分析[J].中国冶金, 2012, 22(11):26-29
|
[4] |
邱雪松, 谭佳梅, 张永锟, 等.热轧酸洗板表面黑色条纹缺陷成因分析[J].中国冶金, 2012, 22(11):26-29
|
[5] |
孙蓟泉, 张帆.带钢表面氧化缺陷的产生于预防[J]. 鞍钢技术, 2013, (2): 1-41.
|
[5] |
孙蓟泉, 张帆.带钢表面氧化缺陷的产生于预防[J]. 鞍钢技术, 2013, (2): 1-41.
|
[6] |
于洋, 唐帅, 郭晓波, 等.热轧卷板氧化铁皮形成机理及控制策略的研究[J].钢铁, 2006, 41(11):50-52
|
[6] |
于洋, 唐帅, 郭晓波, 等.热轧卷板氧化铁皮形成机理及控制策略的研究[J].钢铁, 2006, 41(11):50-52
|
[7] |
徐继根.优化磨削工艺防止轧辊表面振纹[J].轻合金加工技术, 2013, 41(11):35-63
|
[7] |
徐继根.优化磨削工艺防止轧辊表面振纹[J].轻合金加工技术, 2013, 41(11):35-63
|
[8] |
李军.优化轧辊磨削工艺浅谈[J]. 本钢技术, 2006, (3): 31-34.
|
[8] |
李军.优化轧辊磨削工艺浅谈[J]. 本钢技术, 2006, (3): 31-34.
|
[9] |
范伟.轧辊磨削原理简析[J].轻合金加工技术, 2012, 40(4):30-32
|
[9] |
范伟.轧辊磨削原理简析[J].轻合金加工技术, 2012, 40(4):30-32
|
[10] |
王思睿, 周素强, 王连轩.高表面质量带钢轧辊磨削工艺研究[C]// 高表面质量带钢轧辊磨削工艺研究. 年全国钢材深加工研讨会论文集. 302-306.
|
[10] |
王思睿, 周素强, 王连轩.高表面质量带钢轧辊磨削工艺研究[C]// 高表面质量带钢轧辊磨削工艺研究. 年全国钢材深加工研讨会论文集. 302-306.
|
[11] |
郭忠峰.热连轧带钢板型控制与辊型优化设计[D]. 沈阳: 东北大学, 2008.
|
[11] |
郭忠峰.热连轧带钢板型控制与辊型优化设计[D]. 沈阳: 东北大学, 2008.
|
[12] |
梁超.冷轧轧辊磨削研究[J]. 酒钢科技, 2011, (2): 323-327.
|
[12] |
梁超.冷轧轧辊磨削研究[J]. 酒钢科技, 2011, (2): 323-327.
|
[1] |
ZHAO Yun-peng, YU Chao, XIAO Hong, WU Zong-he, XU Peng-peng, XIE Hong-biao. Effect of pure iron interlayer on mechanical properties of hot rolled stainless steel clad plate[J]. Iron and Steel, 2020, 55(5): 73-79. |
[2] |
CAI Zhen, LIANG Wen, WANG Shui-ze, LIU Yong-qian. Discussion about practice and process of ferrite rolling in Ti-IF steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 7-. |
[3] |
ZHOU Cong-rui, CHEN Xiao-long, ZHOU Ming-ke,FAN Lei, MEI Peng, BAO Si-qian. Cause analysis of surface blackening of SPHC hot rolled strip after pickling[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 41-. |
[4] |
SUN Ming-han, ZHENG Yi, QU Chun-tao, JIN Shi-zhe, XU Zhi-qiang, DU Feng-shan. Numerical simulation of temperature field in ultra-fast cooling process of hot rolled plate[J]. Iron and Steel, 2020, 55(3): 50-57. |
[5] |
YANG Geng-wei1,HU Zhuo-li1,YIN Qi-long1,MAO Xin-ping1,2,MIAO Li-sha1,LIU Yang2. Effect of phase transformation time on microstructure and mechanical properties of hotrolled TRIP steel produced by CSP process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 143-149. |
[6] |
YI Ya-li, HAN Xiao-kai, ZHANG Lei, JIN He-rong. Homogeneity of grain structure for 316L/EH40 stainless steel clad plate during hot rolling process[J]. Iron and Steel, 2020, 55(1): 47-55. |
|
|
|
|